BASF Ultrason S 2010 G4 20% Glass Filled PSU
| Category | Polymer , Thermoplastic , Polysulfone (PSU) , Polysulfone, 20% Glass Fiber Reinforced |
| Manufacturer | BASF |
| Trade Name | Ultrason S |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | BASF Ultrason S 2010 G4 20% Glass Filled PSU.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Ultrason S 2010 G4 is a 20% glass reinforced, medium viscosity injection molding PSU grade with high rigidity and strength.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.39 g/cc | 0.0502 lb/in³ | ISO 1183 |
| Water Absorption | 0.70 % | 0.70 % | ISO 62 |
| Moisture Absorption at Equilibrium | 0.20 % | 0.20 % | 23°C/50% R.H.; ISO 62 |
| Viscosity Test | 63 cm³/g | 63 cm³/g | Viscosity number |
| Linear Mold Shrinkage, Flow | 0.0031 cm/cm | 0.0031 in/in | ISO 294 |
| Linear Mold Shrinkage, Transverse | 0.0052 cm/cm | 0.0052 in/in | ISO 294 |
| Melt Flow | 40 g/10 min @Load 10.0 kg, Temperature 360 °C |
40 g/10 min @Load 22.0 lb, Temperature 680 °F |
ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Ball Indentation Hardness | 170 MPa | 24700 psi | ISO 2039-1 |
| Tensile Strength at Break | 110 MPa | 16000 psi | 5mm/min; ISO 527-2 |
| Tensile Strength, Yield | 110 MPa | 16000 psi | 50mm/min; ISO 527-2 |
| Elongation at Break | 2.2 % | 2.2 % | 5mm/min; ISO 527-2 |
| Elongation at Yield | 2.2 % | 2.2 % | 50mm/min; ISO 527-2 |
| Tensile Modulus | 6.80 GPa | 986 ksi | ISO 527-2 |
| Flexural Strength | 164 MPa | 23800 psi | ISO Data |
| Shear Modulus | 0.0250 GPa @Temperature 200 °C |
3.63 ksi @Temperature 392 °F |
ISO 6721 |
| 0.800 GPa @Temperature 175 °C |
116 ksi @Temperature 347 °F |
ISO 6721 | |
| 0.900 GPa @Temperature 100 °C |
131 ksi @Temperature 212 °F |
ISO 6721 | |
| 0.950 GPa @Temperature 50.0 °C |
138 ksi @Temperature 122 °F |
ISO 6721 | |
| Izod Impact, Notched (ISO) | 7.00 kJ/m² | 3.33 ft-lb/in² | ISO 180/A |
| 7.00 kJ/m² @Temperature -30.0 °C |
3.33 ft-lb/in² @Temperature -22.0 °F |
ISO 180/A | |
| Charpy Impact Unnotched | 4.50 J/cm² | 21.4 ft-lb/in² | ISO 179/1eU |
| 4.50 J/cm² @Temperature -30.0 °C |
21.4 ft-lb/in² @Temperature -22.0 °F |
ISO 179/1eU | |
| Charpy Impact, Notched | 0.700 J/cm² | 3.33 ft-lb/in² | ISO 179/1eA |
| 0.750 J/cm² @Temperature -30.0 °C |
3.57 ft-lb/in² @Temperature -22.0 °F |
ISO 179/1eA | |
| Tensile Creep Modulus, 1000 hours | 6000 MPa | 870000 psi | ISO 899 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 26.0 µm/m-°C @Temperature 23.0 - 80.0 °C |
14.4 µin/in-°F @Temperature 73.4 - 176 °F |
ISO 11359-1/-2 |
| 28.0 µm/m-°C @Temperature 140 - 180 °C |
15.6 µin/in-°F @Temperature 284 - 356 °F |
ISO 11359-1/-2 | |
| Maximum Service Temperature, Air | 180 °C | 356 °F | short cycle operations |
| Deflection Temperature at 0.46 MPa (66 psi) | 188 °C | 370 °F | ISO 75 |
| Deflection Temperature at 1.8 MPa (264 psi) | 183 °C | 361 °F | ISO 75 |
| Glass Transition Temp, Tg | 187 °C | 369 °F | ISO 11357-1/-3 |
| UL RTI, Electrical | 160 °C | 320 °F | 50% decrease of tensile strength after 20000h; 746B |
| Flammability, UL94 | V-1 @Thickness 1.60 mm |
V-1 @Thickness 0.0630 in |
|
| V-0 @Thickness 3.20 mm |
V-0 @Thickness 0.126 in |
||
| Oxygen Index | 40 % | 40 % | ISO 4589-1/-2 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | >= 1.00e+13 ohm-cm | >= 1.00e+13 ohm-cm | IEC 60093 |
| Surface Resistance | >= 1.00e+14 ohm | >= 1.00e+14 ohm | IEC 60093 |
| Dielectric Constant | 3.5 @Frequency 100 Hz |
3.5 @Frequency 100 Hz |
IEC 60250 |
| 3.5 @Frequency 1.00e+6 Hz |
3.5 @Frequency 1.00e+6 Hz |
IEC 60250 | |
| Dielectric Strength | 46.0 kV/mm | 1170 kV/in | IEC 60243-1 3 |
| Dissipation Factor | 0.0010 @Frequency 100 Hz |
0.0010 @Frequency 100 Hz |
IEC 60250 |
| 0.0060 @Frequency 1.00e+6 Hz |
0.0060 @Frequency 1.00e+6 Hz |
IEC 60250 | |
| Comparative Tracking Index | 125 V | 125 V | Test liquid A & B; IEC 60112 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 350 - 390 °C | 662 - 734 °F | Injection molding |
| Mold Temperature | 130 - 180 °C | 266 - 356 °F | Injection molding |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Color | Natural and Black | |
| Commercial Status | North America and Europe | |
| Impact Modified | No | |
| Primary Processing Technique | Injection Molding and Extrution |
Users viewing this material also viewed the following:
- Momentive Performance Materials EPC Boron Nitride (BN) Water Based Coating
- Lehmann & Voss LUVOCOM® 1-7893/GY Polyamide 66, with carbon fiber, heat stabilized
- SABIC Innovative Plastics LNP LUBRICOMP RFL36SXC PA 66 (Europe-Africa-Middle East)
- SABIC Innovative Plastics Ultem 1010A PEI (Europe-Africa-Middle East)
- Teknor Apex Sinvicomp SIH 5569 Polyvinyl Chloride, Flexible
- Dow DOWLEX™ 2045.02 Linear Low Density Polyethylene, Heavy Duty Film Grade
- Aclo Accutech Polypropylene Homopolymer HP0339G40CL Glass Reinforced Coupled
- Cast Nylons Nycast® 6PA-Natural Nylon 6, Food Grade
- 3M Scotch® 215 Fine Line Tape
Copyright © lookpolymers.com All Rights Reserved