BASF Ultramid® SEG8 BK-126 40% Glass Filled PA6 (Dry)

Category Polymer , Thermoplastic , Nylon , Nylon 6 , Nylon 6, 40% Glass Fiber Filled
Manufacturer BASF
Trade Name Ultramid®
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF BASF Ultramid® SEG8 BK-126 40% Glass Filled PA6 (Dry).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Ultramid SEG8 BK-126 is a 40% glass reinforced, pigmented black, injection molding type 6 nylon requiring high strength, surface aesthetics, and good processability. This product has excellent surface appearance while maintaining a good balance of physical properties, such as high strength, improved toughness, and chemical resistance. It features superior flow properties, and is suited for parts having thinner walls and those requiring long lengths. It shows lower pressure, temperature, and cycle time requirements than conventional grades.
Physical Properties Metric English Comments
Density 1.45 g/cc
0.0524 lb/in³
ISO 1183
Linear Mold Shrinkage 0.0020 cm/cm
0.0020 in/in
ASTM Data; MD
Mechanical Properties Metric English Comments
Tensile Strength, Ultimate 190 MPa
27600 psi
5mm/min; ISO 527
Elongation at Break 3.0 %
3.0 %
5mm/min; ISO 527
Tensile Modulus 11.0 GPa
1600 ksi
1mm/min; ISO 527
Flexural Modulus 10.74 GPa
1558 ksi
ISO Data
Izod Impact, Notched (ISO) 11.6 kJ/m²
5.52 ft-lb/in²
ISO Test
Thermal Properties Metric English Comments
Melting Point 220 °C
428 °F
10 K/min
220 °C
428 °F
ASTM Test
Deflection Temperature at 0.46 MPa (66 psi) 215 °C
419 °F
ISO 75
Deflection Temperature at 1.8 MPa (264 psi) 205 °C
401 °F
ISO 75
Descriptive Properties Value Comments
Color BK-126
Commercial Status Active America
Impact Modified No
Primary Processing Technique Injection Molding