- HOME
- POLYMER SEARCH
- Thermoplastic
- Polyester, TP
- Polybutylene Terephthalate (PBT)
- Polybutylene Terephthalate (PBT), Unreinforced, Molded
- BASF Ultradur B 4520 BK00110 PBT
BASF Ultradur B 4520 BK00110 PBT
| Category | Polymer , Thermoplastic , Polyester, TP , Polybutylene Terephthalate (PBT) , Polybutylene Terephthalate (PBT), Unreinforced, Molded |
| Manufacturer | BASF |
| Trade Name | Ultradur B |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | BASF Ultradur B 4520 BK00110 PBT.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Ultradur B 4520 BK00110 is a medium viscosity, pigmented black, rapidly freezing injection molding grade.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.30 g/cc | 0.0470 lb/in³ | ISO 1183 |
| Water Absorption | 0.50 % | 0.50 % | ISO 62 |
| Moisture Absorption at Equilibrium | 0.25 % | 0.25 % | 23°C/50% R.H.; ISO 62 |
| Viscosity Test | 119 cm³/g | 119 cm³/g | Viscosity number |
| Linear Mold Shrinkage | 0.015 cm/cm | 0.015 in/in | ASTM Data; MD |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 57.0 MPa | 8270 psi | 50mm/min; ISO 527 |
| 57.0 MPa | 8270 psi | 2 in/min; ASTM Test | |
| Elongation at Yield | 9.6 % | 9.6 % | 2 in/min; ASTM Test |
| 15 % | 15 % | 50mm/min; ISO 527 | |
| Tensile Modulus | 2.40 GPa | 348 ksi | 1mm/min; ISO 527 |
| Flexural Modulus | 2.50 GPa | 363 ksi | ISO Data |
| Izod Impact, Notched (ISO) | 4.80 kJ/m² | 2.28 ft-lb/in² | ISO Test |
| 4.20 kJ/m² @Temperature -40.0 °C |
2.00 ft-lb/in² @Temperature -40.0 °F |
ISO Test | |
| Charpy Impact, Notched | 0.500 J/cm² | 2.38 ft-lb/in² | ISO 179 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Melting Point | 223 °C | 433 °F | 10 K/min |
| 223 °C | 433 °F | ASTM Test | |
| Deflection Temperature at 0.46 MPa (66 psi) | 132 °C | 270 °F | ISO 75 |
| Deflection Temperature at 1.8 MPa (264 psi) | 55.0 °C | 131 °F | ISO 75 |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Color | BK110 | |
| Commercial Status | North America and Europe | |
| Form | Pellets | |
| Impact Modified | No | |
| Primary Processing Technique | Injection Molding | |
| Special characteristic | Heat stabilized or stable to heat | |
| Light stabilized or stable to light | ||
| Lubricant | ||
| U.V. stabilized or stable to weather |
Users viewing this material also viewed the following:
- Network Polymers NPS 90-0645 Super High Impact Polystyrene
- Industrial Laminates/Norplex ES-3 Engraving Stock
- Lubriplate 35 Soluble Oil Metal Working Fluid
- Momentive Performance Materials TUFELâ„¢ II 94605 Low Volatile Extrusion Heat Cured Rubber
- Special Metals Nitinol High-Temperature Shape Memory Ni-Ti alloy
- Shandong Rike Chemical HELIâ„¢ HL-275S PVC Processing Aid Series (PA)
- Dow Corning HV 1650/50 SILICONE RUBBER
- 3M Scotchcal™ ElectroCut™ 7125-57 Graphic Film
- Plenco 50335 PET, Pellet, Injection Molded, Black (discontinued **)
Copyright © lookpolymers.com All Rights Reserved