BASF Ultramid® KR 4355 G7 BK 00564 35% Glass Filled PA6/6T (Conditioned)

Category	Polymer , Thermoplastic , Nylon , Nylon 6 , Nylon 6, 40% Glass Fiber Filled
Manufacturer	BASF
Trade Name	Ultramid®
Port	Shanghai port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	BASF Ultramid® KR 4355 G7 BK 00564 35% Glass Filled PA6/6T (Conditioned).pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

Description: 35% glass-fiber reinforced product for injection-molding; high toughness, strength and stiffness, low water absorption, high melting point (295°C [563°F]). The mechanical properties remain constant after moisture absorption up to a temperature of 60°C [140°F], for instance, for automotive valve housings.Information provided by BASF

Physical Properties	Metric	English	Comments
Bulk Density	0.500 - 0.800 g/cc	0.0181 - 0.0289 lb/in³
Density	1.43 g/cc	0.0517 lb/in³	ISO 1183
Water Absorption	4.3 - 5.3 %	4.3 - 5.3 %	Saturation; ISO 62
Moisture Absorption at Equilibrium	0.80 - 1.2 %	0.80 - 1.2 %	23°C; 50% RH; ISO 62
Viscosity Measurement	130	130	ISO 307
Linear Mold Shrinkage	0.0035 cm/cm	0.0035 in/in	restricted
Linear Mold Shrinkage, Flow	0.0030 cm/cm	0.0030 in/in	ISO 2577
	0.0033 cm/cm	0.0033 in/in	TM=320°C, TW=100°C
Linear Mold Shrinkage, Transverse	0.010 cm/cm	0.010 in/in	ISO 2577

Mechanical Properties	Metric	English	Comments
Tensile Strength, Yield	200 MPa	29000 psi	50 mm/min; ISO 527-1/-2
Tensile Creep Modulus, 1000 hours	8700 MPa @Strain <=0.500 %	1.26e+6 psi @Strain <=0.500 %	ISO 899-1

Thermal Properties	Metric	English	Comments
Thermal Conductivity	0.280 W/m-K	1.94 BTU-in/hr-ft²-°F	DIN 52612
Melting Point	295 °C	563 °F	DIN 53765
Maximum Service Temperature, Air	135 °C	275 °F	for 50% loss of tensile strength after 20000hr
	160 °C	320 °F	for 50% loss of tensile strength after 5000hr
	270 °C	518 °F
Decomposition Temperature	>= 350 °C	>= 662 °F

Electrical Properties	Metric	English	Comments
Volume Resistivity	1.00e+12 ohm-cm	1.00e+12 ohm-cm	IEC 60093
Surface Resistance	1.00e+12 ohm	1.00e+12 ohm	IEC 60093
Dielectric Constant	4.4 @Frequency 1.00 Hz	4.4 @Frequency 1.00 Hz	IEC 60250
Dissipation Factor	0.030 @Frequency 1.00e+6 Hz	0.030 @Frequency 1.00e+6 Hz	IEC 60250
Comparative Tracking Index	600 V	600 V	Test solution A; IEC 60112

Processing Properties	Metric	English	Comments
Zone 1	300 °C	572 °F	Feed Zone
Zone 2	310 °C	590 °F	Compression
Zone 3	320 °C	608 °F	Metering-zone
Zone 4	320 °C	608 °F	Nozzle
Melt Temperature	310 - 330 °C	590 - 626 °F	Injection-molding/Extrusion
	320 °C	608 °F	Optimal
Mold Temperature	80.0 - 120 °C	176 - 248 °F	Injection-molding
	100 °C	212 °F	Optimal
Drying Temperature	110 °C	230 °F
Dry Time	8 hour	8 hour
Moisture Content	<= 0.030 %	<= 0.030 %	Optimal
	<= 0.15 %	<= 0.15 %

Descriptive Properties	Value	Comments
Color	BK 00564
Commercial Status	Europe
Ignition Temperature	>470°C	ASTM D1929