SABIC Innovative Plastics LNP VERTON RV00AE PA 66 (Europe-Africa-Middle East)
| Category | Polymer , Thermoplastic , Nylon , Nylon 66 |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | LNP VERTON |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics LNP VERTON RV00AE PA 66 (Europe-Africa-Middle East).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
LNP* VERTON* RV00AE is a compound based on PA 66 rsin containing Long Glass Fiber. Added features include; Easy Molding.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.58 g/cc | 0.0571 lb/in³ | ISO 1183 |
| Linear Mold Shrinkage, Flow | 0.0015 - 0.0035 cm/cm @Time 86400 sec |
0.0015 - 0.0035 in/in @Time 24.0 hour |
ISO 294 |
| Linear Mold Shrinkage, Transverse | 0.0022 cm/cm @Time 86400 sec |
0.0022 in/in @Time 24.0 hour |
ISO 294 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 265 MPa | 38400 psi | 5 mm/min; ISO 527 |
| Elongation at Break | 1.9 % | 1.9 % | 5 mm/min; ISO 527 |
| Tensile Modulus | 18.38 GPa | 2666 ksi | 1 mm/min; ISO 527 |
| Flexural Strength | 370 MPa | 53700 psi | 2 mm/min; ISO 178 |
| Flexural Modulus | 15.55 GPa | 2255 ksi | 2 mm/min; ISO 178 |
| Izod Impact, Notched (ISO) | 45.0 kJ/m² | 21.4 ft-lb/in² | 80*10*4; ISO 180/1A |
| 38.0 kJ/m² @Temperature -40.0 °C |
18.1 ft-lb/in² @Temperature -40.0 °F |
80*10*4; ISO 180/1A | |
| Izod Impact, Unnotched (ISO) | 89.0 kJ/m² | 42.4 ft-lb/in² | 80*10*4; ISO 180/1U |
| Impact Test | 152 J | 112 ft-lb | Multiaxial Impact; ISO 6603 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 18.6 µm/m-°C @Temperature 23.0 - 60.0 °C |
10.3 µin/in-°F @Temperature 73.4 - 140 °F |
ISO 11359-2 |
| CTE, linear, Transverse to Flow | 67.3 µm/m-°C @Temperature 23.0 - 60.0 °C |
37.4 µin/in-°F @Temperature 73.4 - 140 °F |
ISO 11359-2 |
| Deflection Temperature at 0.46 MPa (66 psi) | 258 °C | 496 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf |
| Deflection Temperature at 1.8 MPa (264 psi) | 253 °C | 487 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
Users viewing this material also viewed the following:
- PolyOne Edgetek® MP-10GF/000 Modified PPO - 10% Glass Fiber Reinforced (discontinued **)
- XXX Phenolic Laminate
- Lubrizol Advanced Materials PEARLTHANE® Clear 15N80 Thermoplastic Polyurethane Elastomer
- Suzhou Hipro Polymers Hiprolon® 200 MC HLS G30 Nylon 1010, 30% glass fiber filled
- Master Bond EP30R Fiber Reinforced Two Component Epoxy Adhesive
- 3M Scotch-Weld™ Hi-Strength Laminating 92 Cylinder Spray Adhesive
- Arkema Group Evatane® 1004 VL 4E Ethylene Vinyl Acetate
- Arlon 55359R062 62 mil Uncured/Cured Silicone Rubber with Fiberglass Substrate
- SABIC Innovative Plastics Lexan® FXE144H PC (Europe-Africa-Middle East)
- SABIC Innovative Plastics NORYL PX2907 PPE+PS (Asia Pacific)
Copyright © lookpolymers.com All Rights Reserved