Physical Properties | Metric | English | Comments |
---|---|---|---|
Bulk Density | 0.500 - 0.800 g/cc | 0.0181 - 0.0289 lb/in³ | |
Density | 1.36 g/cc | 0.0491 lb/in³ | ISO 1183 |
Water Absorption | 5.9 - 6.5 % | 5.9 - 6.5 % | ISO 62 |
Moisture Absorption at Equilibrium | 2.2 - 2.6 % | 2.2 - 2.6 % | ISO 62 |
Viscosity Measurement | 145 | 145 | ISO 307 |
Linear Mold Shrinkage | 0.0075 cm/cm | 0.0075 in/in | |
Melt Flow | 81.6 g/10 min @Load 5.00 kg, Temperature 275 °C |
81.6 g/10 min @Load 11.0 lb, Temperature 527 °F |
ISO 1133 |
Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Tensile Strength at Break | 45.0 MPa | 6530 psi | ISO 527-1/-2 |
Elongation at Break | 45 % | 45 % | ISO 527-1/-2 |
Tensile Modulus | 1.70 GPa | 247 ksi | ISO 527-1/-2 |
Flexural Strength | 50.0 MPa | 7250 psi | ISO 178 |
Flexural Modulus | 1.40 GPa | 203 ksi | ISO 178 |
Izod Impact, Notched (ISO) | 15.0 kJ/m² @Temperature 23.0 °C |
7.14 ft-lb/in² @Temperature 73.4 °F |
ISO 180/1A |
Charpy Impact Unnotched | NB @Temperature 23.0 °C |
NB @Temperature 73.4 °F |
ISO 179/1eU |
Charpy Impact, Notched | 1.80 J/cm² @Temperature 23.0 °C |
8.57 ft-lb/in² @Temperature 73.4 °F |
ISO 179/1eA |
Tensile Creep Modulus, 1000 hours | 800 MPa @Strain <=0.500 % |
116000 psi @Strain <=0.500 % |
ISO 899-1 |
Thermal Properties | Metric | English | Comments |
---|---|---|---|
Thermal Conductivity | 0.310 W/m-K | 2.15 BTU-in/hr-ft²-°F | DIN 52612-1 |
Melting Point | 220 °C | 428 °F | ISO 11357-1/-3 |
Maximum Service Temperature, Air | 100 °C | 212 °F | for 50% loss of tensile strength after 20000hr |
180 °C | 356 °F | ||
Decomposition Temperature | >= 300 °C | >= 572 °F |
Electrical Properties | Metric | English | Comments |
---|---|---|---|
Volume Resistivity | 1.00e+10 ohm-cm | 1.00e+10 ohm-cm | IEC 60093 |
Surface Resistance | 1.00e+10 ohm | 1.00e+10 ohm | IEC 60093 |
Dielectric Constant | 6.2 @Frequency 1.00e+6 Hz |
6.2 @Frequency 1.00e+6 Hz |
IEC 60250 |
Dissipation Factor | 0.20 @Frequency 1.00e+6 Hz |
0.20 @Frequency 1.00e+6 Hz |
IEC 60250 |
Comparative Tracking Index | 450 V | 450 V | Test Solution A; IEC 60112 |
Processing Properties | Metric | English | Comments |
---|---|---|---|
Processing Temperature | 80.0 °C | 176 °F | Hopper Throat |
Zone 1 | 260 °C | 500 °F | Feed Zone |
Zone 2 | 370 °C | 698 °F | Compression |
Zone 3 | 280 °C | 536 °F | Metering-zone |
Zone 4 | 280 °C | 536 °F | Nozzle |
Melt Temperature | 270 - 290 °C | 518 - 554 °F | Injection Molding/Extrusion |
280 °C | 536 °F | Optimal | |
Mold Temperature | 80.0 °C | 176 °F | Optimal |
80.0 - 90.0 °C | 176 - 194 °F | Injection Molding | |
Drying Temperature | 80.0 °C | 176 °F | |
Dry Time | 4 hour | 4 hour |
Descriptive Properties | Value | Comments |
---|---|---|
Color | BK 23213 | |
Commercial Status | Europe | |
Ignition Temperature | >400°C | ASTM D1929 |
Peripheral screw speed | < 0.3 m/s |