ExxonMobil Escorene® LD 755.CM Molding, extrusion and compounding resin

Category	Polymer , Thermoplastic , Ethylene Vinyl Acetate , Ethylene Vinyl Acetate Copolymer (EVA), Extrusion/Coating Grade
Manufacturer	Exxon Chemical
Trade Name	Escorene®
Port	Ningbo port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	ExxonMobil Escorene® LD 755.CM Molding, extrusion and compounding resin.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

Escorene Ultra LD 755.CM is a high vinyl acetate copolymer for specialty compounding applications and hot melt adhesives.Availability: Latin America, North America and South America Additive: Antiblock: NoSlip: NoThermal Stabilizer: Yes Applications:CompoundingHot Melt AdhesivesMaster Base ResinInformation provided by ExxonMobil Chemical

Physical Properties	Metric	English	Comments
Density	0.952 g/cc	0.0344 lb/in³	ExxonMobil Method
Vinyl Acetate Content	27.6 %	27.6 %	ExxonMobil Method
Melt Flow	25.0 g/10 min @Load 2.16 kg, Temperature 190 °C	25.0 g/10 min @Load 4.76 lb, Temperature 374 °F	ASTM D1238

Mechanical Properties	Metric	English	Comments
Hardness, Shore A	70	70	15s; ASTM D2240
Hardness, Shore D	19	19	15s; ASTM D2240
Tensile Strength at Break	4.83 MPa	700 psi	ASTM D638
Elongation at Break	>= 800 %	>= 800 %	ASTM D638
Flexural Modulus	0.0186 GPa	2.70 ksi	1% secant; ASTM D790
Impact Test	14.9 J @Temperature 23.0 °C	11.0 ft-lb @Temperature 73.4 °F	Instrument Impact, Total Energy; ASTM D3763
	25.8 J @Temperature -40.0 °C	19.0 ft-lb @Temperature -40.0 °F	Instrumented Impact, Total Energy; ASTM D3763

Thermal Properties	Metric	English	Comments
Melting Point	66.1 °C	151 °F	Peak Melting Temperature; ExxonMobil Method