BASF Ultramid® B3L PA6 (Conditioned)
| Category | Polymer , Thermoplastic , Nylon , Nylon 6 , Nylon 6, Impact Grade |
| Manufacturer | BASF |
| Trade Name | Ultramid® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | BASF Ultramid® B3L PA6 (Conditioned).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Ultramid B3L is an impact-modified, easy flowing injection molding PA6 grade for fast processing.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.10 g/cc | 0.0397 lb/in³ | ISO 1183 |
| Water Absorption | 8.5 - 9.5 % | 8.5 - 9.5 % | ISO 62 |
| Moisture Absorption at Equilibrium | 2.1 - 2.9 % | 2.1 - 2.9 % | (23°C/50% R.H.); ISO 62 |
| Melt Flow | 121 g/10 min @Load 5.00 kg, Temperature 275 °C |
121 g/10 min @Load 11.0 lb, Temperature 527 °F |
ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 35.0 MPa | 5080 psi | 50mm/min; ISO 527 |
| Elongation at Yield | 18 % | 18 % | 50mm/min; ISO 527 |
| Modulus of Elasticity | 0.900 GPa | 131 ksi | ISO 527 |
| Izod Impact, Notched (ISO) | NB | NB | ISO 180/A |
| Charpy Impact Unnotched | NB | NB | ISO 179/1eU |
| Charpy Impact, Notched | NB | NB | ISO 179/1eA |
| Tensile Creep Modulus, 1000 hours | 550 MPa | 79800 psi | ISO 899 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Heat Capacity | 1.50 J/g-°C | 0.359 BTU/lb-°F | |
| Thermal Conductivity | 0.320 W/m-K | 2.22 BTU-in/hr-ft²-°F | DIN 52612 |
| Melting Point | 220 °C | 428 °F | DIN 53765 |
| Maximum Service Temperature, Air | 160 °C | 320 °F |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 1.00e+10 ohm-cm | 1.00e+10 ohm-cm | IEC 60093 |
| Surface Resistance | 1.00e+10 ohm | 1.00e+10 ohm | IEC 60093 |
| Dielectric Constant | 6.4 @Frequency 1.00e+6 Hz |
6.4 @Frequency 1.00e+6 Hz |
IEC 60250 |
| Dissipation Factor | 0.24 @Frequency 1.00e+6 Hz |
0.24 @Frequency 1.00e+6 Hz |
IEC 60250 |
| Comparative Tracking Index | 600 V | 600 V | Test Solution A; IEC 60112 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 250 - 270 °C | 482 - 518 °F | Injection-molding/Extrusion |
| Mold Temperature | 40.0 - 80.0 °C | 104 - 176 °F | Injection-molding |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Color | Natural | |
| Commercial Status | North America and Europe | |
| Form | Pellets | |
| Impact Modified | Yes | |
| Primary Processing Technique | Injection Molding | |
| Processing | Injection Molding | |
| Special characteristic | Heat stabilized or stable to heat | |
| Release agent |
Users viewing this material also viewed the following:
- Polimeri Europa SINKRAL PD H210/K ABS (discontinued **)
- Pau Tai Unistab BC-600 Mixed Metal Liquid Stabilizer for PVC Cadmium/Barium/Zinc Self-Lubricating
- MarkeTech Repton 201 Aluminum Oxide
- Mateck Neodymium Gallate Substrate, NdGaO3
- LG Chemical LUPOS GP2200 ABS+GF20%, General Purpose
- SABIC Innovative Plastics Noryl EN130S PPE+HIPS (Europe-Africa-Middle East)
- The NanoSteel® Company SHS 9172 HVOF Steel Alloy, Atomized Powder
- Polyplastics FR-PET® B3045FA Glass Fiber Reinforced Polyethylene Terephthalate (GF-PET), Slow burning, General purpose
- Tipco Tipcolite® TX 321 Phenolic Compound, Wood Flour & Minerals, having Soft Flow & High Electrical Properties
- Colorite Polymers 6575 General Purpose Vinyl Compound
Copyright © lookpolymers.com All Rights Reserved