BASF Ultramid® B3EG6 LS BK 23189 30% Glass Filled PA6 (Conditioned)
| Category | Polymer , Thermoplastic , Nylon , Nylon 6 , Nylon 6, 30% Glass Fiber Filled |
| Manufacturer | BASF |
| Trade Name | Ultramid® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | BASF Ultramid® B3EG6 LS BK 23189 30% Glass Filled PA6 (Conditioned).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Information provided by BASF
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Bulk Density | 0.500 - 0.800 g/cc | 0.0181 - 0.0289 lb/in³ | |
| Density | 1.36 g/cc | 0.0491 lb/in³ | ISO 1183 |
| Water Absorption | 6.3 - 6.9 % | 6.3 - 6.9 % | ISO 62 |
| Moisture Absorption at Equilibrium | 1.9 - 2.3 % | 1.9 - 2.3 % | ISO 62 |
| Viscosity Measurement | 140 | 140 | ISO 307 |
| Linear Mold Shrinkage | 0.0035 cm/cm | 0.0035 in/in | |
| Melt Flow | 68 g/10 min @Load 5.00 kg, Temperature 275 °C |
68 g/10 min @Load 11.0 lb, Temperature 527 °F |
ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 115 MPa | 16700 psi | ISO 527-1/-2 |
| Elongation at Break | 8.0 % | 8.0 % | ISO 527-1/-2 |
| Tensile Modulus | 6.20 GPa | 899 ksi | ISO 527-1/-2 |
| Flexural Strength | 180 MPa | 26100 psi | ISO 178 |
| Flexural Modulus | 5.00 GPa | 725 ksi | ISO 178 |
| Izod Impact, Notched (ISO) | 20.0 kJ/m² @Temperature 23.0 °C |
9.52 ft-lb/in² @Temperature 73.4 °F |
ISO 180/1A |
| Charpy Impact Unnotched | 11.0 J/cm² @Temperature 23.0 °C |
52.3 ft-lb/in² @Temperature 73.4 °F |
ISO 179/1eU |
| Charpy Impact, Notched | 3.00 J/cm² @Temperature 23.0 °C |
14.3 ft-lb/in² @Temperature 73.4 °F |
ISO 179/1eA |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Thermal Conductivity | 0.360 W/m-K | 2.50 BTU-in/hr-ft²-°F | DIN 52612-1 |
| Melting Point | 220 °C | 428 °F | ISO 11357-1/-3 |
| Maximum Service Temperature, Air | 135 °C | 275 °F | for 50% loss of tensile strength after 20000hr |
| 165 °C | 329 °F | for 50% loss of tensile strength after 5000hr | |
| 200 °C | 392 °F | ||
| Decomposition Temperature | >= 300 °C | >= 572 °F |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 1.00e+10 ohm-cm | 1.00e+10 ohm-cm | IEC 60093 |
| Surface Resistance | 1.00e+10 ohm | 1.00e+10 ohm | IEC 60093 |
| Dielectric Constant | 6.8 @Frequency 1.00e+6 Hz |
6.8 @Frequency 1.00e+6 Hz |
IEC 60250 |
| Dissipation Factor | 0.022 @Frequency 1.00e+6 Hz |
0.022 @Frequency 1.00e+6 Hz |
IEC 60250 |
| Comparative Tracking Index | 575 V | 575 V | Test Solution A; IEC 60112 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 270 - 290 °C | 518 - 554 °F | Injection Molding/Extrusion |
| Mold Temperature | 80.0 - 90.0 °C | 176 - 194 °F | Injection Molding |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Commercial Status | Europe | |
| Ignition Temperature | >400°C | ASTM D1929 |
Users viewing this material also viewed the following:
- Precision Polymer Engineering V72G Fluoroelastomer Compound
- Solvay Engineered Polymers INDURE™ X190 TPO (discontinued **)
- SABIC Innovative Plastics LNP LUBRICOMP EX10404H PEI
- Sibur ABS 1106 Extrusion Grade ABS Plastic
- Teijin Panlite® BN-8110R Improved Mold Release, Carbon Fiber Reinforced, Flame Resistant Polycarbonate Resin
- DuPont Elvaloy® 2615 AC Ethylene and 15% Ethyl Acrylate Copolymer
- Dow Corning FZ-3196 Caprylyl Methicone
- Cossa Polimeri ESTADIENE 0425 GFS Acrylonitrile Butadiene Styrene, 13% Glass Filled
- ChevronTexaco B Soluble Oil
- Ashley Polymers Ashlene® 527-43G Nylon 66, 43% Glass Reinforced
Copyright © lookpolymers.com All Rights Reserved