Chosun Refractories PT-170 Plastic Refractory
| Category | Ceramic , Oxide , Aluminum Oxide |
| Manufacturer | Chosun Refractories |
| Trade Name | |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Chosun Refractories PT-170 Plastic Refractory.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Information provided by Chosun Refractories via Korea Institute of Ceramic Engineering and Technology (KICET).
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Modulus of Rupture | 3.85e-7 - 0.000981 GPa @Temperature 110 °C, Time 86400 sec |
0.0000558 - 0.142 ksi @Temperature 230 °F, Time 24.0 hour |
|
| 0.002943 - 0.005886 GPa @Temperature 1350 °C, Time 10800 sec |
0.4269 - 0.8537 ksi @Temperature 2460 °F, Time 3.00 hour |
||
| 0.0034335 - 0.0063765 GPa @Temperature 1500 °C, Time 10800 sec |
0.49799 - 0.92485 ksi @Temperature 2730 °F, Time 3.00 hour |
||
| Compressive Strength | 4.90 - 9.81 MPa @Temperature 110 °C, Time 86400 sec |
711 - 1420 psi @Temperature 230 °F, Time 24.0 hour |
Cold Crushing Strength |
| 14.7 - 24.5 MPa @Temperature 1350 °C, Time 10800 sec |
2130 - 3560 psi @Temperature 2460 °F, Time 3.00 hour |
Cold Crushing Strength | |
| 19.6 - 29.4 MPa @Temperature 1500 °C, Time 10800 sec |
2840 - 4270 psi @Temperature 2730 °F, Time 3.00 hour |
Cold Crushing Strength |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Thermal Conductivity | 1.0236 W/m-K @Temperature 500 °C |
7.0921 BTU-in/hr-ft²-°F @Temperature 932 °F |
|
| 1.1399 W/m-K @Temperature 1000 °C |
7.8980 BTU-in/hr-ft²-°F @Temperature 1830 °F |
||
| Maximum Service Temperature, Air | 1700 °C | 3090 °F | limited |
| Shrinkage | -0.900 % @Temperature 1500 °C, Time 10800 sec |
-0.900 % @Temperature 2730 °F, Time 3.00 hour |
|
| -0.600 % @Temperature 110 °C, Time 86400 sec |
-0.600 % @Temperature 230 °F, Time 24.0 hour |
||
| -0.100 % @Temperature 1350 °C, Time 10800 sec |
-0.100 % @Temperature 2460 °F, Time 3.00 hour |
| Component Elements Properties | Metric | English | Comments |
|---|---|---|---|
| Al2O3 | 63 % | 63 % | |
| SiO2 | 32 % | 32 % |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Main Applications | Various furnace | |
| Material Required for Estimating (kg/?) | 2,500 |
Users viewing this material also viewed the following:
- SABIC Innovative Plastics LNP LUBRICOMP IP004Z PA6.12 (Europe-Africa-Middle East)
- Sumitomo Chemical ESPOLEX® 4675 Thermoplastic Elastomer
- Tipco Tipcolite® TPG 1214 - Furfural Modified Phenolic Resin with 43mm Norton Flow with 9% Hexamine
- Total PPH 3270 Polypropylene Homopolymer, High Crystallinity, Low Melt Flow Film Grade
- A. Schulman POLYFORT™ FPP 1842 Homopolymer Polypropylene
- Hexcel® HexWeb® HRH-10 - 3/16 - 2.0 Aramid Fiber/Phenolic Resin Honeycomb
- Esstech X-726-0000 PEG 400 Extended Urethane Dimethacrylate, C54H98N4O21
- Asahi Glass Fluon® P-830UP PFA Perfluoropolymer
- SABIC Innovative Plastics Lexan® 945W PC (Asia Pacific)
Copyright © lookpolymers.com All Rights Reserved