BASF Ultramid® 8233G HS 33% Glass Filled PA6 (Conditioned)

Category Polymer , Thermoplastic , Nylon , Nylon 6 , Nylon 6, 30% Glass Fiber Filled
Manufacturer BASF
Trade Name Ultramid®
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF BASF Ultramid® 8233G HS 33% Glass Filled PA6 (Conditioned).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Ultramid 8233G HS is a heat stabilized, 33% glass fiber reinforced nylon 6 molding compound offering excellent strength, stiffness, high temperature performance and dimensional stability. It is also available in non-heat stabilized and/or pigmented versions.
Physical Properties Metric English Comments
Density 1.136 g/cc
0.04104 lb/in³
Melt; ISO 1183
1.39 g/cc
0.0502 lb/in³
dry; ISO 1183
Water Absorption 1.1 %
1.1 %
24 hour; ISO Test
6.4 %
6.4 %
beginning dry; ISO 62
Moisture Absorption at Equilibrium 1.8 %
1.8 %
beginning dry (23°C/50% R.H.); ISO 62
Relative Viscosity 2.6 cP
2.6 cP
ISO Test; 96 % SAV
Viscosity Measurement 50
50
Formic Acid
Linear Mold Shrinkage 0.0030 cm/cm
0.0030 in/in
ASTM Data; MD
Mechanical Properties Metric English Comments
Tensile Strength at Break 125 MPa
18100 psi
0.2 in/min; ASTM Test
60.0 MPa

@Temperature 120 °C
8700 psi

@Temperature 248 °F
ISO Data
60.0 MPa

@Temperature 120 °C
8700 psi

@Temperature 248 °F
ASTM Test
80.0 MPa

@Temperature 80.0 °C
11600 psi

@Temperature 176 °F
ASTM Test
80.0 MPa

@Temperature 80.0 °C
11600 psi

@Temperature 176 °F
ISO Data
255 MPa

@Temperature -40.0 °C
37000 psi

@Temperature -40.0 °F
ASTM Test
255 MPa

@Temperature -40.0 °C
37000 psi

@Temperature -40.0 °F
ISO Data
Tensile Strength, Ultimate 125 MPa
18100 psi
5mm/min; ISO 527
Elongation at Break 6.0 %
6.0 %
5mm/min; ISO 527
6.0 %
6.0 %
0.2 in/min; ASTM Test
3.5 %

@Temperature -40.0 °C
3.5 %

@Temperature -40.0 °F
ASTM Test
3.5 %

@Temperature -40.0 °C
3.5 %

@Temperature -40.0 °F
ISO Data
6.0 %

@Temperature 120 °C
6.0 %

@Temperature 248 °F
ISO Data
6.0 %

@Temperature 80.0 °C
6.0 %

@Temperature 176 °F
ISO Data
6.0 %

@Temperature 120 °C
6.0 %

@Temperature 248 °F
ASTM Test
6.0 %

@Temperature 80.0 °C
6.0 %

@Temperature 176 °F
ASTM Test
Tensile Modulus 5.84 GPa
847 ksi
1mm/min; ISO 527
3.40 GPa

@Temperature 120 °C
493 ksi

@Temperature 248 °F
ISO Data
4.30 GPa

@Temperature 80.0 °C
624 ksi

@Temperature 176 °F
ISO Data
11.6 GPa

@Temperature -40.0 °C
1680 ksi

@Temperature -40.0 °F
ISO Data
Flexural Strength 130 MPa
18900 psi
ISO Data
179 MPa
26000 psi
ASTM Test
361 MPa

@Temperature -40.0 °C
52400 psi

@Temperature -40.0 °F
ASTM Test
Flexural Modulus 5.13 GPa
744 ksi
ASTM Test
5.20 GPa
754 ksi
ISO Data
Izod Impact, Notched 1.07 J/cm

@Temperature -40.0 °C
2.00 ft-lb/in

@Temperature -40.0 °F
ASTM Test
2.35 J/cm

@Thickness 3.17 mm
4.40 ft-lb/in

@Thickness 0.125 in
ASTM Test
Thermal Properties Metric English Comments
Specific Heat Capacity 2.434 J/g-°C
0.5817 BTU/lb-°F
Melt
Thermal Conductivity 0.275 W/m-K
1.91 BTU-in/hr-ft²-°F
Melt
Melting Point 220 °C
428 °F
10 K/min
220 °C
428 °F
ASTM Test
Descriptive Properties Value Comments
Color Natural
Commercial Status Active America
Form Pellets
Impact Modified No
Primary Processing Technique Injection Molding
Processing Injection Molding
Special characteristic Heat stabilized or stable to heat
UL.UL-C Yes