BASF Ultramid® 8202C HS PA6 (Conditioned)

Category	Polymer , Thermoplastic , Nylon , Nylon 6 , Nylon 6, Unreinforced, Flame Retardant
Manufacturer	BASF
Trade Name	Ultramid®
Port	Shanghai port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	BASF Ultramid® 8202C HS PA6 (Conditioned).pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

Ultramid 8202C HS is a heat stabilized, low viscosity, PA6 injection molding homopolymer possessing a modified crystalline structure for increased property performance and faster cycles. It is also available in pigmented versions.

Physical Properties	Metric	English	Comments
Density	1.13 g/cc	0.0408 lb/in³	dry; ISO 1183
Water Absorption	1.6 %	1.6 %	24 hour; ISO Test
	9.3 %	9.3 %	beginning dry; ISO 62
Moisture Absorption at Equilibrium	2.6 %	2.6 %	beginning dry (23°C/50% R.H.); ISO 62
Relative Viscosity	2.6 cP	2.6 cP	ISO Test; 96 % SAV
Viscosity Measurement	48	48	Formic Acid
Linear Mold Shrinkage	0.0090 cm/cm	0.0090 in/in	ASTM Data; MD

Mechanical Properties	Metric	English	Comments
Tensile Strength at Break	70.0 MPa	10200 psi	0.2 in/min; ASTM Test
	20.0 MPa @Temperature 120 °C	2900 psi @Temperature 248 °F	ISO Data
	20.0 MPa @Temperature 120 °C	2900 psi @Temperature 248 °F	ASTM Test
	30.0 MPa @Temperature 80.0 °C	4350 psi @Temperature 176 °F	ASTM Test
	30.0 MPa @Temperature 80.0 °C	4350 psi @Temperature 176 °F	ISO Data
	80.0 MPa @Temperature -40.0 °C	11600 psi @Temperature -40.0 °F	ASTM Test
	80.0 MPa @Temperature -40.0 °C	11600 psi @Temperature -40.0 °F	ISO Data
Tensile Strength, Yield	43.0 MPa	6240 psi	50mm/min; ISO 527
	48.0 MPa	6960 psi	2 in/min; ASTM Test
	25.0 MPa @Temperature 120 °C	3630 psi @Temperature 248 °F	ISO Data
	25.0 MPa @Temperature 120 °C	3630 psi @Temperature 248 °F	ASTM Test
	30.0 MPa @Temperature 80.0 °C	4350 psi @Temperature 176 °F	ASTM Test
	30.0 MPa @Temperature 80.0 °C	4350 psi @Temperature 176 °F	ISO Data
	142 MPa @Temperature -40.0 °C	20600 psi @Temperature -40.0 °F	ASTM Test
	142 MPa @Temperature -40.0 °C	20600 psi @Temperature -40.0 °F	ISO Data
Elongation at Break	>= 50 %	>= 50 %	50mm/min, Nominal strain; ISO 527
	>= 100 %	>= 100 %	2 in/min; ASTM Test
	>= 100 %	>= 100 %
	3.0 % @Temperature -40.0 °C	3.0 % @Temperature -40.0 °F	ASTM Test
	3.0 % @Temperature -40.0 °C	3.0 % @Temperature -40.0 °F	ISO Data
	>= 100 % @Temperature 120 °C	>= 100 % @Temperature 248 °F	ISO Data
	>= 100 % @Temperature 80.0 °C	>= 100 % @Temperature 176 °F	ISO Data
	>= 100 % @Temperature 120 °C	>= 100 % @Temperature 248 °F	ASTM Test
Elongation at Yield	22 %	22 %	50mm/min; ISO 527
	22 %	22 %	2 in/min; ASTM Test
	3.0 % @Temperature -40.0 °C	3.0 % @Temperature -40.0 °F	ASTM Test
	3.0 % @Temperature -40.0 °C	3.0 % @Temperature -40.0 °F	ISO Data
	25 % @Temperature 80.0 °C	25 % @Temperature 176 °F	ISO Data
	25 % @Temperature 80.0 °C	25 % @Temperature 176 °F	ASTM Test
	30 % @Temperature 120 °C	30 % @Temperature 248 °F	ASTM Test
	30 % @Temperature 120 °C	30 % @Temperature 248 °F	ISO Data
Tensile Modulus	1.36 GPa	197 ksi	1mm/min; ISO 527
Flexural Strength	42.0 MPa	6090 psi	ASTM Test
	168 MPa @Temperature -40.0 °C	24400 psi @Temperature -40.0 °F	ASTM Test
Flexural Modulus	0.970 GPa	141 ksi	ASTM Test
Izod Impact, Notched	0.210 J/cm @Temperature -40.0 °C	0.393 ft-lb/in @Temperature -40.0 °F	ASTM Test
	1.71 J/cm @Thickness 3.17 mm	3.20 ft-lb/in @Thickness 0.125 in	ASTM Test

Thermal Properties	Metric	English	Comments
Melting Point	220 °C	428 °F	10 K/min
	220 °C	428 °F	ASTM Test

Processing Properties	Metric	English	Comments
Melt Temperature	260 °C	500 °F	Injection molding
Mold Temperature	80.0 °C	176 °F	Injection molding

Descriptive Properties	Value	Comments
Color	Natural
Commercial Status	Active America
Form	Pellets
Impact Modified	No
Primary Processing Technique	Injection Molding
Processing	Injection Molding
Special characteristic	Heat stabilized or stable to heat
UL.UL-C	Yes