BASF Ultramid® 1603-2 NF2004 43% Glass Filled PA66 (Dry)
| Category | Polymer , Thermoplastic , Nylon , Nylon 66 , Nylon 66, 40% Glass Fiber Filled |
| Manufacturer | BASF |
| Trade Name | Ultramid® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | BASF Ultramid® 1603-2 NF2004 43% Glass Filled PA66 (Dry).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Ultramid 1603-2 NF2004 is a 43% glass reinforced, heat stabilized injection molding nylon 6/6 with the highest level of glass reinforcement for maximum strength and stiffness.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.50 g/cc | 0.0542 lb/in³ | ISO 1183 |
| Water Absorption | 4.8 % | 4.8 % | ISO 62 |
| Moisture Absorption at Equilibrium | 1.4 % | 1.4 % | 23°C/50% R.H.; ISO 62 |
| Linear Mold Shrinkage | 0.0030 cm/cm | 0.0030 in/in | ASTM Data; MD |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 234 MPa | 33900 psi | 0.2 in/min; ASTM Test |
| Tensile Strength, Ultimate | 235 MPa | 34100 psi | 5mm/min; ISO 527 |
| Elongation at Break | 3.0 % | 3.0 % | 5mm/min; ISO 527 |
| 3.0 % | 3.0 % | 0.2 in/min; ASTM Test | |
| Tensile Modulus | 13.8 GPa | 2000 ksi | 1mm/min; ISO 527 |
| Flexural Strength | 331 MPa | 48000 psi | ASTM Test |
| Flexural Modulus | 11.0 GPa | 1600 ksi | ASTM Test |
| 12.9 GPa | 1870 ksi | ISO Data | |
| Izod Impact, Notched | 1.39 J/cm @Thickness 3.17 mm |
2.60 ft-lb/in @Thickness 0.125 in |
ASTM Test |
| Izod Impact, Notched (ISO) | 16.0 kJ/m² | 7.61 ft-lb/in² | ISO Test |
| Charpy Impact Unnotched | 10.0 J/cm² | 47.6 ft-lb/in² | ISO 179 |
| 8.00 J/cm² @Temperature -30.0 °C |
38.1 ft-lb/in² @Temperature -22.0 °F |
ISO 179 | |
| Charpy Impact, Notched | 1.60 J/cm² | 7.61 ft-lb/in² | ISO 179 |
| 1.40 J/cm² @Temperature -30.0 °C |
6.66 ft-lb/in² @Temperature -22.0 °F |
ISO 179 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Melting Point | 257 °C | 495 °F | 10 K/min |
| 257 °C | 495 °F | ASTM Test | |
| Deflection Temperature at 0.46 MPa (66 psi) | 264 °C | 507 °F | ISO 75 |
| Deflection Temperature at 1.8 MPa (264 psi) | 253 °C | 487 °F | ASTM Test |
| 256 °C | 493 °F | ISO 75 |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Color | Natural | |
| Commercial Status | Active America | |
| Impact Modified | No | |
| Primary Processing Technique | Injection Molding |
Users viewing this material also viewed the following:
- Phillips 66 COPYLENE® CM500LN Polypropylene, Impact Copolymer, High Flow, Medium Impact, Nucleated, Lube, Injection Molding
- Lehmann & Voss LUVOCOM® 1105-0904/GN PEEK, with glass fiber
- CLAL-MSX NICLAL 1300 H12 1/2 Hard Copper Alloy, Free Cutting Nickel-Silver
- A. Schulman ComAlloy Aqualoy® 125 Polypropylene, Glass Reinforced, Chemically Coupled NSF, UL
- A. Schulman ComAlloy Comtuf® 522 Polycarbonate/Styrenic Alloy
- Schmolz + Bickenbach Cryodur® 2510 (O-1) Cold Work Die Steel
- Solvay TECHNYL® A 20 V25 PA66, 25% glass fiber, DRY
- Unipetrol Grade F Diesel Oil
- Sharadaa Ceramics 0.4 Insulation Brick
Copyright © lookpolymers.com All Rights Reserved