BASF Ultramid® 1603-2 NF2004 43% Glass Filled PA66 (Conditioned)
| Category | Polymer , Thermoplastic , Nylon , Nylon 66 , Nylon 66, 40% Glass Fiber Filled |
| Manufacturer | BASF |
| Trade Name | Ultramid® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | BASF Ultramid® 1603-2 NF2004 43% Glass Filled PA66 (Conditioned).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Ultramid 1603-2 NF2004 is a 43% glass reinforced, heat stabilized injection molding nylon 6/6 with the highest level of glass reinforcement for maximum strength and stiffness.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.50 g/cc | 0.0542 lb/in³ | dry; ISO 1183 |
| Water Absorption | 4.8 % | 4.8 % | beginning dry; ISO 62 |
| Moisture Absorption at Equilibrium | 1.4 % | 1.4 % | beginning dry (23°C/50% R.H.); ISO 62 |
| Linear Mold Shrinkage | 0.0030 cm/cm | 0.0030 in/in | ASTM Data; MD |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Ultimate | 167 MPa | 24200 psi | 5mm/min; ISO 527 |
| Elongation at Break | 4.0 % | 4.0 % | 5mm/min; ISO 527 |
| Tensile Modulus | 11.0 GPa | 1600 ksi | 1mm/min; ISO 527 |
| Flexural Modulus | 9.00 GPa | 1310 ksi | ISO Data |
| Izod Impact, Notched (ISO) | 17.0 kJ/m² | 8.09 ft-lb/in² | ISO Test |
| Charpy Impact Unnotched | 10.0 J/cm² | 47.6 ft-lb/in² | ISO 179 |
| 8.70 J/cm² @Temperature -30.0 °C |
41.4 ft-lb/in² @Temperature -22.0 °F |
ISO 179 | |
| Charpy Impact, Notched | 1.80 J/cm² | 8.57 ft-lb/in² | ISO 179 |
| 1.50 J/cm² @Temperature -30.0 °C |
7.14 ft-lb/in² @Temperature -22.0 °F |
ISO 179 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Melting Point | 257 °C | 495 °F | 10 K/min |
| 257 °C | 495 °F | ASTM Test |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Color | Natural | |
| Commercial Status | Active America | |
| Impact Modified | No | |
| Primary Processing Technique | Injection Molding |
Users viewing this material also viewed the following:
- Lubrizol Advanced Materials Pearlstick® 45-50/05 Linear Thermoplastic Polyurethane Elastomer (discontinued **
- Ravago Manufacturing Americas Hylon® N1000STHLUV2 HF Nylon 6/6 (discontinued **)
- DuPont Performance Polymers Zytel® 157HSL BK010 Nylon 612 (Unverified Data**)
- Ineos ABS TRIAX® 1120 ABS/Nylon Blend, Injection Grade, As Conditioned
- Sylvin Technologies 8950-65 Natural PVC Extrusion Compound
- Wieland Bio Porta 1020 Solder
- Covestro Baydur® STR/C-400 BB Polyurethane Composite SRIM Foam, 60% Glass Filled, MDI-based 2-Component Liquid System
- DuPont Performance Polymers Delrin® SC655 NC010 Acetal (POM) (Unverified Data**)
- Hippe PF CC 41 Woven Cotton Cloth Reinforced Phenolic Resin - Round, Molded Tube and Rod
Copyright © lookpolymers.com All Rights Reserved