BASF Ultramid® 1503-2 NF2004 33% Glass Filled PA66 (Conditioned)
| Category | Polymer , Thermoplastic , Nylon , Nylon 66 , Nylon 66, 30% Glass Fiber Filled |
| Manufacturer | BASF |
| Trade Name | Ultramid® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | BASF Ultramid® 1503-2 NF2004 33% Glass Filled PA66 (Conditioned).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Ultramid 1503-2 NF2004 is a 33% glass reinforced, heat stabilized injection molding PA6/6.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.40 g/cc | 0.0506 lb/in³ | dry; ISO 1183 |
| Water Absorption | 5.7 % | 5.7 % | beginning dry; ISO 62 |
| Moisture Absorption at Equilibrium | 1.7 % | 1.7 % | beginning dry (23°C/50% R.H.); ISO 62 |
| Linear Mold Shrinkage | 0.0030 cm/cm | 0.0030 in/in | ASTM Data; MD |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Ultimate | 145 MPa | 21000 psi | 5mm/min; ISO 527 |
| Elongation at Break | 5.0 % | 5.0 % | 5mm/min; ISO 527 |
| Tensile Modulus | 7.40 GPa | 1070 ksi | 1mm/min; ISO 527 |
| Flexural Modulus | 6.30 GPa | 914 ksi | ISO Data |
| Izod Impact, Notched (ISO) | 15.0 kJ/m² | 7.14 ft-lb/in² | ISO Test |
| Charpy Impact Unnotched | 10.0 J/cm² | 47.6 ft-lb/in² | ISO 179 |
| 7.50 J/cm² @Temperature -30.0 °C |
35.7 ft-lb/in² @Temperature -22.0 °F |
ISO 179 | |
| Charpy Impact, Notched | 1.50 J/cm² | 7.14 ft-lb/in² | ISO 179 |
| 1.10 J/cm² @Temperature -30.0 °C |
5.24 ft-lb/in² @Temperature -22.0 °F |
ISO 179 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Melting Point | 257 °C | 495 °F | 10 K/min |
| 257 °C | 495 °F | ASTM Test |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Color | Natural | |
| Commercial Status | Active America | |
| Impact Modified | No | |
| Primary Processing Technique | Injection Molding |
Users viewing this material also viewed the following:
- Nilit FRIANYL B63 TF20 Nylon 6 for injection molding, 20% PTFE lubricated
- Radici Radilon® S 37FL T Nylon 6
- Polymer Resources PC/TP-GP2 PC Polyester, High Impact, Excellent Chemical Resistance (Unverified Data**)&
- Less Common Metals Cerium Vacuum Remelted Rare Earth Metal
- Special Metals INCONEL® 690 Nickel Superalloy, Cold Drawn Tube, 0.75 inch (19.0 mm) o.d. and 0.065 inch (1.65 mm) Thickness
- Saint-Gobain CHR® SG25-05(R) Primary Glass-PTFE Backing Silicone Adhesive Pressure Sensitive Tape
- Teknor Apex Telcar® TL-1050-75 Thermoplastic Elastomer
- Hexcel® HexForce™ 1614 Fiber Glass Fabric
- CMW® D505F Silver Nickel Contact Material
Copyright © lookpolymers.com All Rights Reserved