BASF Ultraform N 2320 U017 UNC Q600 POM
| Category | Polymer , Thermoplastic , Acetal (POM) , Acetal Copolymer, Unreinforced |
| Manufacturer | BASF |
| Trade Name | Ultraform N |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | BASF Ultraform N 2320 U017 UNC Q600 POM.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Ultraform N 2320 U017 UNC Q600 is a UV stabilized rapidly freezing injection-molding POM grade.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.41 g/cc | 0.0509 lb/in³ | ISO 1183 |
| Linear Mold Shrinkage | 0.020 cm/cm | 0.020 in/in | ASTM Data; MD |
| Melt Flow | 9.0 g/10 min @Load 2.16 kg, Temperature 190 °C |
9.0 g/10 min @Load 4.76 lb, Temperature 374 °F |
ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 61.0 MPa | 8850 psi | 50mm/min; ISO 527 |
| 61.0 MPa | 8850 psi | 2 in/min; ASTM Test | |
| Elongation at Break | >= 50 % | >= 50 % | 50mm/min, Nominal strain; ISO 527 |
| Elongation at Yield | 11 % | 11 % | 50mm/min; ISO 527 |
| 11 % | 11 % | 2 in/min; ASTM Test | |
| Tensile Modulus | 2.60 GPa | 377 ksi | 1mm/min; ISO 527 |
| Charpy Impact, Notched | 0.600 J/cm² | 2.86 ft-lb/in² | ISO 179 |
| 0.600 J/cm² @Temperature -30.0 °C |
2.86 ft-lb/in² @Temperature -22.0 °F |
ISO 179 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 150 °C | 302 °F | ISO 75 |
| Deflection Temperature at 1.8 MPa (264 psi) | 90.0 °C | 194 °F | ISO 75 |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Color | Natural | |
| Commercial Status | Active America | |
| Impact Modified | No | |
| Primary Processing Technique | Injection Molding |
Users viewing this material also viewed the following:
- Park Electrochemical Nelcote® V-341 Polybutadiene Prepreg, 503 Quartz Reinforced
- Fiberfil® J-60/20/E8/M Polypropylene Homopolymer, 20% Glass Reinforced, Chemically coupled
- Kingfa MAC-751 PC/ABS Alloy
- SYNTHOS Krasten® 154 General Purpose Polystyrene
- Techmer ES Plastiblend® PA6 HS L MB Nylon 6
- SCG Chemicals EL-Leneâ„¢ H6670B High Density Polyethylene Film
- A. Schulman PAPERMATCH® T-4448/50 Specialty Masterbatch
- A. Schulman SCHULADUR® A GF33HI 33% Glass Fiber Reinforced, High Impact PBT
- Zircar Zirconia ZYK-15 Zirconia Cloth Insulation
- Arlon 37N Polyimide Low-Flow
Copyright © lookpolymers.com All Rights Reserved