BASF Ultradur® S 4090 G4X 20% Glass Filled PBT

Category Polymer , Thermoplastic , ASA Polymer , Polyester, TP , Polybutylene Terephthalate (PBT) , PBT + ASA Blend, Glass Fiber Reinforced
Manufacturer BASF
Trade Name Ultradur®
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF BASF Ultradur® S 4090 G4X 20% Glass Filled PBT.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Description: Is a PBT + ASA, low-warpage, free-flowing injection-molding grades with very good processing capabilities, containing 20% of glass fibers for industrial parts with high dimensional stability, for example internal components for vehicles, plug connectors and housings.Information provided by BASF
Physical Properties Metric English Comments
Density 1.39 g/cc
0.0502 lb/in³
ISO 1183
Water Absorption 0.40 %
0.40 %
Saturation; DIN 53495/1L
Moisture Absorption at Equilibrium 0.20 %
0.20 %
23°C; 50% RH
Viscosity Measurement 104
104
[ml/g]; Viscosity number; ISO 1628
Linear Mold Shrinkage, Flow 0.0020 cm/cm
0.0020 in/in
Sheet
0.0046 cm/cm
0.0046 in/in
60x60x2 mm; ISO 294
Linear Mold Shrinkage, Transverse 0.0091 cm/cm
0.0091 in/in
60x60x2 mm; ISO 294
0.010 cm/cm
0.010 in/in
Sheet
Melt Flow 41.7 g/10 min

@Load 2.16 kg,
Temperature 275 °C
41.7 g/10 min

@Load 4.76 lb,
Temperature 527 °F
ISO 1133
Mechanical Properties Metric English Comments
Tensile Strength, Yield 100 MPa
14500 psi
50 mm/min; ISO 527-2
Elongation at Yield 2.6 %
2.6 %
50 mm/min; ISO 527-2
Modulus of Elasticity 6.80 GPa
986 ksi
ISO 527-2
Charpy Impact Unnotched 4.90 J/cm²
23.3 ft-lb/in²
ISO 179/1eU
Charpy Impact, Notched 0.660 J/cm²
3.14 ft-lb/in²
ISO 179/1eA
Thermal Properties Metric English Comments
Melting Point 220 - 225 °C
428 - 437 °F
DSC; ISO 11357-3
Deflection Temperature at 0.46 MPa (66 psi) 210 °C
410 °F
ISO 75-2
Deflection Temperature at 1.8 MPa (264 psi) 190 °C
374 °F
ISO 75-2
Processing Properties Metric English Comments
Melt Temperature 260 - 280 °C
500 - 536 °F
Injection-molding
270 °C
518 °F
for shrinkage test
Mold Temperature 60.0 - 80.0 °C
140 - 176 °F
80.0 °C
176 °F
for shrinkage test
Descriptive Properties Value Comments
Color Natural and Black
Commercial Status Europe
Primary Processing Technique Injection Molding