- Lehmann & Voss LUVOCOM® 1105-0706 PEEK, with glass fiber
Lehmann & Voss LUVOCOM® 1105-0706 PEEK, with glass fiber
| Category | Polymer , Thermoplastic , Polyketone , Polyetheretherketone (PEEK) , Polyetheretherketone, PEEK, Glass Fiber Filled |
| Manufacturer | Lehmann & Voss & Co. |
| Trade Name | LUVOCOM® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Lehmann & Voss LUVOCOM® 1105-0706 PEEK, with glass fiber.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Applications: Automotive industry, textile machinery, medical- and precision engineering, aircraft industry.Strong, stiff parts; impact resistance.Dynamic stressed parts at high movement velocity.Chemical and hydrolysis resistance parts, non flammable.High dimensionally stable precision parts, high continuous use temperature.Bearings, sleeves, control disks, gear wheels, pump impellers, gear parts.Information provided by Lehmann & Voss & Co.KG
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.49 g/cc | 1.49 g/cc | ISO 1183 |
| Water Absorption | <= 0.10 % | <= 0.10 % | 23°C/24h |
| Linear Mold Shrinkage | 0.0030 - 0.0070 cm/cm | 0.0030 - 0.0070 in/in |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Stress | 170 MPa | 24700 psi | |
| Elongation at Yield | 3.5 % | 3.5 % | |
| 4.5 % | 4.5 % | flexural | |
| Modulus of Elasticity | 10.0 GPa | 1450 ksi | |
| Flexural Strength | 250 MPa | 36300 psi | |
| Flexural Modulus | 7.00 GPa | 1020 ksi | |
| Charpy Impact Unnotched | 6.00 J/cm² | 28.6 ft-lb/in² | flatwise; ISO 179 1fU |
| 5.50 J/cm² @Temperature -30.0 °C |
26.2 ft-lb/in² @Temperature -22.0 °F |
ISO 179 | |
| Coefficient of Friction, Dynamic | 0.30 | 0.30 | |
| Coefficient of Friction, Static | 0.28 | 0.28 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 21.0 µm/m-°C | 11.7 µin/in-°F | DIN 53752 |
| Thermal Conductivity | 0.350 W/m-K | 2.43 BTU-in/hr-ft²-°F | DIN 52612 |
| Maximum Service Temperature, Air | 250 °C | 482 °F | |
| 280 °C | 536 °F | short term | |
| Deflection Temperature at 1.8 MPa (264 psi) | 315 °C | 599 °F | |
| Vicat Softening Point | 320 °C | 608 °F | DIN ISO 306 |
| Flammability, UL94 | V-0 | V-0 | not recognized by UL |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Insulation Resistance | >= 1.00e+12 ohm | >= 1.00e+12 ohm |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Processing Temperature | 390 °C | 734 °F | mass temp |
| Nozzle Temperature | 360 - 380 °C | 680 - 716 °F | |
| Zone 1 | 360 - 370 °C | 680 - 698 °F | |
| Zone 2 | 380 - 390 °C | 716 - 734 °F | |
| Zone 3 | 390 - 400 °C | 734 - 752 °F | |
| Mold Temperature | 170 - 200 °C | 338 - 392 °F | |
| Drying Temperature | 120 °C @Time 21600 - 28800 sec |
248 °F @Time 6.00 - 8.00 hour |
or |
| 150 °C @Time 10800 - 21600 sec |
302 °F @Time 3.00 - 6.00 hour |
Dehumidifying dryer |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Color | natural color |
Users viewing this material also viewed the following:
- Nye Lubricants 702A-EP (NG) Synthetic Oil
- Quadrant EPP TIVAR® DS PE-UHMW + additives (ISO Data)
- SABIC Innovative Plastics Lexan® HP4R PC
- Phillips 66 COPYLENE® CH005 Polypropylene, Homopolymer, Extrusion, Strapping
- Huntsman Araldite XU 3917 Water-Based Adhesive/Coating
- SABIC Innovative Plastics LNP LUBRICOMP OL004 PPS - Linear
- Solvay Specialty Polymers Hyflon® MFA® P6010 Perfluoropolymer
- CLAL-MSX NICLAFOR® 1000 TF Quenched/Precipitation Heat Treated, Rolled Copper Alloy
- Axiall 12802 Wire & Cable Flexible PVC
- SABIC Innovative Plastics SABIC STAMAX 20YM240 PP
Copyright © lookpolymers.com All Rights Reserved