| Category | Metal , Metal Matrix Composite , Nonferrous Metal , Aluminum Alloy |
| Manufacturer | Materion |
| Trade Name | |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Materion AMC225XE T4 Aluminum/Silicon Carbide MMC Extruded Bar.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Aluminium alloy 2124 reinforced with 25 volume % silicon carbide particles (average size 3 micron). It is manufactured by a powder metallurgy route using high-energy mixing to ensure excellent particle distribution and to
enhance mechanical properties. Good machinability - use diamond tools and high feed/speed for best results.Information provided by Aerospace Metal Composites Limited (AMC).
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 2.88 g/cc | 0.104 lb/in³ |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Brinell | 210 | 210 | Converted from Vickers |
| Hardness, Rockwell A | 58.3 | 58.3 | Converted from Vickers |
| Hardness, Rockwell B | 95 | 95 | Converted from Vickers |
| Hardness, Vickers | 210 | 210 | Pryamidal Diamond 10 kg load |
| Tensile Strength, Ultimate | 690 MPa | 100000 psi | statistical analysis gives AVG -3STD at 626 MPa |
| Tensile Strength, Yield | 487 MPa @Strain 0.200 % |
70600 psi @Strain 0.200 % |
statistical analysis gives AVG-3STD at 438 MPa |
| Elongation at Break | 5.0 % | 5.0 % | in 25 mm |
| Modulus of Elasticity | 115 GPa | 16700 ksi | In Tension |
| Poissons Ratio | 0.30 | 0.30 | |
| Fatigue Strength | 210 MPa @# of Cycles 100000 |
30500 psi @# of Cycles 100000 |
R=0.1, Kt=2.5 |
| 350 MPa @# of Cycles 1.00e+7 |
50800 psi @# of Cycles 1.00e+7 |
RB R=-1 | |
| 400 MPa @# of Cycles 100000 |
58000 psi @# of Cycles 100000 |
R=-1, Kt=1 | |
| Fracture Toughness | 18.0 - 20.0 MPa-m½ | 16.4 - 18.2 ksi-in½ | |
| Shear Modulus | 44.0 GPa | 6380 ksi | Esimated from similar metals. |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 15.5 µm/m-°C @Temperature -100 - 100 °C |
8.61 µin/in-°F @Temperature -148 - 212 °F |
|
| Specific Heat Capacity | 0.836 J/g-°C | 0.200 BTU/lb-°F | |
| Thermal Conductivity | 150 W/m-K @Temperature 0.000 - 100 °C |
1040 BTU-in/hr-ft²-°F @Temperature 32.0 - 212 °F |
|
| Melting Point | 548 - 660 °C | 1020 - 1220 °F | |
| Solidus | 548 °C | 1020 °F | |
| Liquidus | 660 °C | 1220 °F |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Electrical Resistivity | 0.00000900 ohm-cm | 0.00000900 ohm-cm |
Users viewing this material also viewed the following:
- MV Labs ZR800 Zr(SO4)2·xH2O Zirconium(IV) sulfate hydrate (low Hf)
- Process Technologies Inc Viton® Extreme™ Compound 2001 Sanitary Gasket/O-Ring
- SABIC Innovative Plastics LNP Faradex AS0039 ABS (Europe-Africa-Middle East)
- Haynes Ultimet® alloy, aged 1000 hours at 649°C (1200°F)
- SK Chemicals SKYTHANE® U1753C Ink Binder
- SABIC Innovative Plastics LNP THERMOCOMP WFB33E PBT (Europe-Africa-Middle East)
- Westlake Plastics Ardel® Polyarylate
- Zeon Chemicals Nipol® DN003 Nitrile Elastomer
Copyright © lookpolymers.com All Rights Reserved