BASF Ultradur B 4406 G6 Q113 30% Glass Filled PBT

Category Polymer , Thermoplastic , Polyester, TP , Polybutylene Terephthalate (PBT) , Polybutylene Terephthalate (PBT), Glass Fiber Filled, Flame Retardant
Manufacturer BASF
Trade Name Ultradur B
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF BASF Ultradur B 4406 G6 Q113 30% Glass Filled PBT.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Ultradur B4406 G6 Q113 is an UL V0 injection molding, PBT grade with 30% glass fiber reinforcement.
Physical Properties Metric English Comments
Density 1.68 g/cc
0.0607 lb/in³
ISO 1183
Water Absorption 0.40 %
0.40 %
ISO 62
Moisture Absorption at Equilibrium 0.20 %
0.20 %
23°C/50% R.H.; ISO 62
Viscosity Test 105 cm³/g
105 cm³/g
Viscosity number
Linear Mold Shrinkage 0.0030 cm/cm
0.0030 in/in
ASTM Data; MD
Linear Mold Shrinkage, Flow 0.0028 cm/cm
0.0028 in/in
ISO Data
Linear Mold Shrinkage, Transverse 0.0094 cm/cm
0.0094 in/in
ISO Data
Melt Flow 19 g/10 min

@Load 2.16 kg,
Temperature 275 °C
 19 g/10 min

@Load 4.76 lb,
Temperature 527 °F
 ISO 1133
Mechanical Properties Metric English Comments
Tensile Strength, Ultimate 135 MPa
19600 psi
5mm/min; ISO 527
Elongation at Break 2.1 %
2.1 %
5mm/min; ISO 527
Tensile Modulus 11.5 GPa
1670 ksi
1mm/min; ISO 527
Charpy Impact Unnotched 5.00 J/cm²
23.8 ft-lb/in²
ISO 179
Charpy Impact, Notched 0.800 J/cm²
3.81 ft-lb/in²
ISO 179
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 28.0 µm/m-°C
15.6 µin/in-°F
ISO 11359
Melting Point 223 °C
433 °F
10 K/min
223 °C
433 °F
ASTM Test
Deflection Temperature at 0.46 MPa (66 psi) 220 °C
428 °F
ISO 75
Deflection Temperature at 1.8 MPa (264 psi) 195 °C
383 °F
ISO 75
Flammability, UL94 V-0

@Thickness 1.60 mm
 V-0

@Thickness 0.0630 in
V-0

@Thickness 0.800 mm
 V-0

@Thickness 0.0315 in
Electrical Properties Metric English Comments
Volume Resistivity >= 1.00e+13 ohm-cm
>= 1.00e+13 ohm-cm
IEC 60093
Surface Resistance >= 1.00e+15 ohm
>= 1.00e+15 ohm
IEC 60093
Dielectric Constant 3.7

@Frequency 1.00e+6 Hz
 3.7

@Frequency 1.00e+6 Hz
 IEC 60250
3.9

@Frequency 100 Hz
 3.9

@Frequency 100 Hz
 IEC 60250
Dissipation Factor 0.0014

@Frequency 100 Hz
 0.0014

@Frequency 100 Hz
 IEC 60250
0.0158

@Frequency 1.00e+6 Hz
 0.0158

@Frequency 1.00e+6 Hz
 IEC 60250
Comparative Tracking Index 200 V
200 V
IEC 60112
Descriptive Properties Value Comments
Color Natural
Commercial Status North America and Europe
Form Pellets
Impact Modified No
Primary Processing Technique Injection Molding
Processing Injection Molding
Special characteristic Flame retarding agent
Heat stabilized or stable to heat
Light stabilized or stable to light
Lubricant
U.V. stabilized or stable to weather