BASF Novolen® 3248 TC Polypropylene
| Category | Polymer , Thermoplastic , Polypropylene (PP) , Polypropylene, Molded |
| Manufacturer | BASF |
| Trade Name | Novolen® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | BASF Novolen® 3248 TC Polypropylene.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Easy-flowing grade containing nucleating and antistatic agents for transparent injection molded parts.Data was collected by ISO methods and provided by BASF.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.910 g/cc | 0.0329 lb/in³ | |
| Water Absorption | 0.10 % | 0.10 % | |
| Moisture Absorption at Equilibrium | 0.10 % | 0.10 % | |
| Linear Mold Shrinkage, Flow | 0.013 cm/cm | 0.013 in/in | |
| Melt Flow | 65 g/10 min @Load 2.16 kg, Temperature 230 °C |
65 g/10 min @Load 4.76 lb, Temperature 446 °F |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 29.0 MPa | 4210 psi | |
| Elongation at Break | >= 50 % | >= 50 % | |
| Elongation at Yield | 11 % | 11 % | |
| Tensile Modulus | 1.15 GPa | 167 ksi | |
| Charpy Impact Unnotched | 18.0 J/cm² | 85.7 ft-lb/in² | |
| 1.20 J/cm² @Temperature -30.0 °C |
5.71 ft-lb/in² @Temperature -22.0 °F |
||
| Charpy Impact, Notched | 0.400 J/cm² | 1.90 ft-lb/in² | |
| 0.130 J/cm² @Temperature -30.0 °C |
0.619 ft-lb/in² @Temperature -22.0 °F |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 185 µm/m-°C @Temperature 20.0 °C |
103 µin/in-°F @Temperature 68.0 °F |
|
| Melting Point | 150 °C | 302 °F | |
| Deflection Temperature at 0.46 MPa (66 psi) | 70.0 °C | 158 °F | |
| Deflection Temperature at 1.8 MPa (264 psi) | 50.0 °C | 122 °F | |
| Vicat Softening Point | 72.0 °C | 162 °F |
| Optical Properties | Metric | English | Comments |
|---|---|---|---|
| Transmission, Visible | 90 % | 90 % | transparent; thickness not quantified |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Electrical Resistivity | 1.00e+14 ohm-cm | 1.00e+14 ohm-cm | |
| Surface Resistance | 1.00e+10 ohm | 1.00e+10 ohm | |
| Dielectric Constant | 2.3 @Frequency 1e+6 Hz |
2.3 @Frequency 1e+6 Hz |
|
| Dielectric Strength | 140 kV/mm | 3560 kV/in | |
| Dissipation Factor | 0.00081 @Frequency 100 Hz |
0.00081 @Frequency 100 Hz |
|
| 0.0020 @Frequency 1e+6 Hz |
0.0020 @Frequency 1e+6 Hz |
||
| Comparative Tracking Index | 600 V | 600 V |
Users viewing this material also viewed the following:
- Nanocyl PLASTICYL™ PP2001 Polypropylene with 2 wt% Multi-Wall Carbon Nanotubes
- Overview of materials for Polybutylene Terephthalate (PBT), 50% Glass Fiber Filled
- H.C. Starck Amperit® 825.1 Zirconium Oxide-Yttrium Oxide 93-7 (ZrO2-Y2O3)
- Hong Kun Group 6-Bromo-2-methylquinoline Pharmaceutical Intermediate
- Solvay TECHNYL® SSD 330 KNF/E PA66, 15% glass filled, DRY
- SABIC Innovative Plastics ULTEM 2210R PEI (Asia Pacific)
- Wellman Wellamid® XT1668-BK1 High Impact Nylon 66
- TSE Industries Millathane® 76 Millable Polyester Polyurethane Rubber, 3.0 PHR Luperco 130XL Peroxide
- Daelim H&L Plavis-G15 CM 15% Graphite Filled Aromatic Polyimide Bearing
Copyright © lookpolymers.com All Rights Reserved