BASF Elastollan B 60 A WHA TPUR

Category	Polymer , Thermoplastic , Polyurethane, TP , Thermoplastic Polyurethane (TPUR), Polyester Grade
Manufacturer	BASF
Trade Name	Elastollan
Port	Ningbo port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	BASF Elastollan B 60 A WHA TPUR.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

Description: Thermoplastic Polyester Polyurethane Elastomers with excellent mechanical properties, outstanding wear resistance, high tensile strength, good damping and resilience performance and superior low temperature flexibility.Typical Applications: Sport-shoe soles and accessories, ski-boot shells, technical moldings, e.g. seals, castor tyres and tubing.Note: Quoted results are from measurements on injection molded test platens, post tempered for 20 hours at 100°CInformation provided by BASF

Physical Properties	Metric	English	Comments
Density	1.17 g/cc	0.0423 lb/in³	ISO 1183-1-A

Mechanical Properties	Metric	English	Comments
Hardness, Shore A	60	60	ISO 868
Tensile Strength	20.0 MPa	2900 psi	after storage in water at 80°C for 42 days; ISO 37
	35.0 MPa	5080 psi	ISO 37
	1.00 MPa @Strain 20.0 %	145 psi @Strain 20.0 %	ISO 37
	2.50 MPa @Strain 100 %	363 psi @Strain 100 %	ISO 37
	6.50 MPa @Strain 300 %	943 psi @Strain 300 %	ISO 37
Elongation at Break	900 %	900 %	ISO 37
	1000 %	1000 %	after storage in water at 80°C for 42 days; ISO 37
Charpy Impact, Notched	NB @Temperature -30.0 °C	NB @Temperature -22.0 °F	DIN EN ISO 179
	NB @Temperature 23.0 °C	NB @Temperature 73.4 °F	DIN EN ISO 179
Tear Strength	50.0 kN/m	285 pli	DIN ISO 34-1/Bb
Abrasion	40	40	[mm<sup>3</sup>; ISO 4649
Compression Set	20 % @Temperature 23.0 °C	20 % @Temperature 73.4 °F	ISO 815
	30 % @Temperature 70.0 °C	30 % @Temperature 158 °F	ISO 815

Processing Properties	Metric	English	Comments
Processing Temperature	175 - 230 °C	347 - 446 °F	Injection molding
Mold Temperature	20.0 - 70.0 °C	68.0 - 158 °F

Descriptive Properties	Value	Comments
Commercial Status	North America
Primary Processing Technique	Injection molding

Users viewing this material also viewed the following: