BASF Elastollan® 685A15N Polyester Type Polyurethane Elastomer

Category Polymer , Thermoplastic , Elastomer, TPE , Polyurethane, TP , Thermoplastic Polyurethane, Elastomer, Polyester Grade
Manufacturer BASF
Trade Name Elastollan®
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF BASF Elastollan® 685A15N Polyester Type Polyurethane Elastomer.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
This grade is FDA compliant, section 177.2600 and 177.1680, for both wet and dry contact with food. The Elastollan 600 Series of products listed are products that are part of a new series of polyester-based thermoplastic polyurethanes (TPU). They are specifically formulated for extruded profile, sheet and film applications. They exhibit excellent abrasion resistance, toughness and transparency. With respect to processing they are generally easy to process and have a very wide processing window. In some cases it is as high as 25 to 30°C. As with all TPU products this grade must be dried prior to processing.Property values below are typical values based on molded plaques cured 20 hours at 100°C before testing. Information provided by BASF Corporation.
Physical Properties Metric English Comments
Density 1.21 g/cc
0.0437 lb/in³
ASTM D792
Mechanical Properties Metric English Comments
Hardness, Shore A 85
85
ASTM D2240
Tensile Strength, Ultimate 31.3 MPa
4540 psi
ASTM D412
Tensile Strength, Yield 6.30 MPa

@Strain 100 %
914 psi

@Strain 100 %
ASTM D-412
12.8 MPa

@Strain 300 %
1860 psi

@Strain 300 %
ASTM D-412
Elongation at Break 655 %
655 %
ASTM D412
Tear Strength 90.0 kN/m
514 pli
ASTM D624
Taber Abrasion, mg/1000 Cycles 25
25
H-18 wheel; ASTM D-1044.
Processing Properties Metric English Comments
Drying Temperature 80.0 - 90.0 °C
176 - 194 °F
Must be dried. Typical condition.
Dry Time 2 - 4 hour
2 - 4 hour
Moisture Content <= 0.030 %
<= 0.030 %