Azoty Tarnow™ TARNOFORM 500 GF6 POM

Category Polymer , Thermoplastic , Acetal (POM) , Acetal Copolymer, 30% Glass Fiber Reinforced
Manufacturer Azoty Tarnow™ (Zaklady Azotowe)
Trade Name TARNOFORM
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Azoty Tarnow™ TARNOFORM 500 GF6 POM.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
30% glass fiber reinforced, high flow injection molding grade, suitable for applications where high strength and stiffness is required, combined with higher flowability during molding.Information provided by Zakłady Azotowe w Tarnowie-Moscicach S.A.
Physical Properties Metric English Comments
Density 1.63 g/cc
0.0589 lb/in³
ISO 1183
Water Absorption 0.50 %
0.50 %
23°C/24 hr; ISO 62
Linear Mold Shrinkage 0.0102 cm/cm
0.0102 in/in
60x60x4
Linear Mold Shrinkage, Transverse 0.018 cm/cm
0.018 in/in
ISO 294-4
Melt Flow 9.5 g/10 min

@Load 2.16 kg,
Temperature 190 °C
9.5 g/10 min

@Load 4.76 lb,
Temperature 374 °F
ISO 1133
Mechanical Properties Metric English Comments
Ball Indentation Hardness 239 MPa
34700 psi
358 N; ISO 2039-1
Tensile Strength at Break 99.0 MPa
14400 psi
ISO 527
Elongation at Break 1.3 %
1.3 %
ISO 527
Tensile Modulus 10.25 GPa
1487 ksi
ISO 527
Flexural Strength 149 MPa
21600 psi
ISO 178
Flexural Modulus 9.65 GPa
1400 ksi
ISO 178
Izod Impact, Notched (ISO) 5.80 kJ/m²
2.76 ft-lb/in²
1A; ISO 180
Charpy Impact, Notched 0.510 J/cm²
2.43 ft-lb/in²
1eA; ISO 179
Thermal Properties Metric English Comments
Specific Heat Capacity 1.21 J/g-°C
0.289 BTU/lb-°F
Melting Point 167 °C
333 °F
10°C/min.; ISO 3146
Maximum Service Temperature, Air 110 °C
230 °F
Deflection Temperature at 1.8 MPa (264 psi) 163 °C
325 °F
ISO 75
Vicat Softening Point 158 °C
316 °F
50 N; ISO 306
Flammability, UL94 HB

@Thickness 3.20 mm
HB

@Thickness 0.126 in
Electrical Properties Metric English Comments
Volume Resistivity 1.00e+14 ohm-cm
1.00e+14 ohm-cm
IEC 60093
Surface Resistance 1.00e+13 ohm
1.00e+13 ohm
IEC 60093
Dielectric Constant 4.2

@Frequency 100 Hz
4.2

@Frequency 100 Hz
IEC 60250
4.2

@Frequency 1e+6 Hz
4.2

@Frequency 1e+6 Hz
IEC 60250
Dielectric Strength 30.0 kV/mm
762 kV/in
IEC 60243
Dissipation Factor 0.0095

@Frequency 1e+6 Hz
0.0095

@Frequency 1e+6 Hz
IEC 60250
Comparative Tracking Index 600 V
600 V
IEC 112
Processing Properties Metric English Comments
Processing Temperature 180 - 230 °C
356 - 446 °F
Barrel temperature
Mold Temperature 60.0 - 120 °C
140 - 248 °F