Azdel Plus R300-B01 30% Continuous Random Fiber Mat / PP Resin Matrix

Category	Polymer , Thermoplastic , Polypropylene (PP)
Manufacturer	Azdel
Trade Name	Plus
Port	Ningbo port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	Azdel Plus R300-B01 30% Continuous Random Fiber Mat / PP Resin Matrix.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

AZDEL® R300-B01 is a glass mat thermoplastic laminate based upon a random oriented continuous fiber mat contained within a polypropylene resin matrix. This composite material features high flow properties and a very homogeneous fiber distribution. This material is typically used for standard semi-structural applications where high stiffness and impact are desired.Mechanical properties and mold shrinkage measured on flat plaques.Information provided by Azdel.

Physical Properties	Metric	English	Comments
Specific Gravity	1.10 g/cc	1.10 g/cc	Laminate; ASTM D792
	1.14 g/cc	1.14 g/cc	Molded; ASTM D792
Filler Content	30 %	30 %	By weight (ashing); Internal
Thickness	3900 microns	154 mil	Sheet; Internal
Linear Mold Shrinkage	0.0020 - 0.0040 cm/cm	0.0020 - 0.0040 in/in	Measured on flat plaques; ASTM D955

Mechanical Properties	Metric	English	Comments
Tensile Strength at Break	60.0 MPa	8700 psi	ISO 527
Elongation at Break	2.2 %	2.2 %	ISO 527
Tensile Modulus	4.30 GPa	624 ksi	ISO 527
Flexural Strength	110 MPa	16000 psi	ISO 178
Flexural Modulus	4.40 GPa	638 ksi	ISO 178
Impact	3800 @Thickness 4.00 mm	3800 @Thickness 0.157 in	Multi-axial in Newtons, at max. force; ASTM D3763
Impact Test	10.0 J @Thickness 4.00 mm	7.38 ft-lb @Thickness 0.157 in	Multi-axial, at max. load; ASTM D3763
	28.0 J @Thickness 4.00 mm	20.7 ft-lb @Thickness 0.157 in	Multi-axial, at failure; ASTM D3763

Thermal Properties	Metric	English	Comments
Deflection Temperature at 1.8 MPa (264 psi)	155 °C	311 °F	ASTM D648

Descriptive Properties	Value	Comments
Color	Black	Internal