- Asia International Enterprise (Hong Kong) 30G3F Polybutylene terephthalate, 15% Glass Fiber Filled
Asia International Enterprise (Hong Kong) 30G3F Polybutylene terephthalate, 15% Glass Fiber Filled
| Category | Polymer , Thermoplastic , Polyester, TP , Polybutylene Terephthalate (PBT) , Polybutylene Terephthalate (PBT), 20% Glass Fiber Filled , Polybutylene Terephthalate (PBT), Flame Retardant |
| Manufacturer | Asia Int'l Enterprise (Hong Kong) Limited |
| Trade Name | |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Asia International Enterprise (Hong Kong) 30G3F Polybutylene terephthalate, 15% Glass Fiber Filled.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Information provided by Asia International Enterprise (Hong Kong) Ltd.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.51 g/cc @Temperature 23.0 °C |
1.51 g/cc @Temperature 73.4 °F |
ASTM D792 |
| Filler Content | 15 % | 15 % | |
| Linear Mold Shrinkage | 0.0050 - 0.012 cm/cm | 0.0050 - 0.012 in/in | ASTM D955 |
| Melt Flow | 19 g/10 min @Load 2.16 kg, Temperature 250 °C |
19 g/10 min @Load 4.76 lb, Temperature 482 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Ultimate | 98.1 MPa | 14200 psi | 5mm/min; ASTM D638 |
| Elongation at Break | 4.0 % | 4.0 % | 5mm/min; ASTM D638 |
| Flexural Strength | 152 MPa | 22000 psi | 2.8mm/min; ASTM D790 |
| Flexural Modulus | 5.88 GPa | 853 ksi | 2.8mm/min; ASTM D790 |
| Izod Impact, Notched | 0.588 J/cm @Thickness 3.17 mm, Temperature 23.0 °C |
1.10 ft-lb/in @Thickness 0.125 in, Temperature 73.4 °F |
ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 210 °C | 410 °F | ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 200 °C | 392 °F | ASTM D648 |
| Flammability, UL94 | V-0 @Thickness 1.50 mm |
V-0 @Thickness 0.0591 in |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Middle Barrel Temperature | 230 - 265 °C | 446 - 509 °F | Cylinder Temperature |
| Mold Temperature | 50.0 - 100 °C | 122 - 212 °F | |
| Drying Temperature | 120 - 140 °C | 248 - 284 °F | |
| Dry Time | 3 - 5 hour | 3 - 5 hour |
Users viewing this material also viewed the following:
- SABIC Innovative Plastics Lexan® FXD921A PC (Europe-Africa-Middle East)
- Lehmann & Voss LUVOCOM® 80-7655/RD Polyacetal-copolymer, with aramid reinforcement and PTFE, toughness-modified, high viscosity
- KKPC KOSYN 1502G Styrene Butadiene Rubber
- Lehmann & Voss PLASLUBE NY-1/TF/20/BK Polyamide 66, with PTFE
- SABIC Innovative Plastics SABIC STAMAX 30YM243 PP
- Teknor Apex Telcar® TL-6800-64 Thermoplastic Elastomer
- Wellman Wellamid® MRGST1715-WBK1 Nylon 6, 25% Mineral and Glass Sphere Reinforced, Impact Modified, Weatherable Grade
- ExxonMobil Exceed™ 1018HA Metallocene Polyethylene Resin (European Grade)
- Colorite Polymers CS7559LS Wire and Cable Insulation Vinyl Compound
- E-Polymers TEKAMID® JN920 PPE+PA66 20% Glass Fiber Reinforced PA/PPE Alloy
Copyright © lookpolymers.com All Rights Reserved