Ashley Polymers Ashlene® P1021R Polycarbonate
| Category | Polymer , Thermoplastic , Polycarbonate (PC) , Polycarbonate, Molded |
| Manufacturer | Ashley Polymers |
| Trade Name | Ashlene® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Ashley Polymers Ashlene® P1021R Polycarbonate.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
A prime general purpose injection molding grade, natural resin with easy mold release.Data provided by the manufacturer
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.20 g/cc | 0.0434 lb/in³ | ASTM D792 |
| Water Absorption | 0.15 % | 0.15 % | ASTM D570 |
| Moisture Absorption at Equilibrium | 0.34 % | 0.34 % | ASTM D570 |
| Linear Mold Shrinkage | 0.0060 cm/cm | 0.0060 in/in | ASTM D955 |
| Melt Flow | 15 - 17 g/10 min | 15 - 17 g/10 min | Cond. 300/1.2 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell M | 70 | 70 | ASTM D785 |
| Hardness, Rockwell R | 118 | 118 | ASTM D785 |
| Tensile Strength, Ultimate | 66.0 MPa | 9570 psi | ATSM D638 |
| Elongation at Break | 120 % | 120 % | ASTM D638 |
| Elongation at Yield | 6.0 % | 6.0 % | ASTM D638 |
| Flexural Modulus | 2.30 GPa | 334 ksi | ASTM D790 |
| Compressive Yield Strength | 76.0 MPa | 11000 psi | ASTM D695 |
| Izod Impact, Notched | 7.48 J/cm | 14.0 ft-lb/in | ASTM D256 |
| Tensile Impact Strength | 580 kJ/m² @Thickness 3.20 mm |
276 ft-lb/in² @Thickness 0.126 in |
ASTM D1822S |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 128 °C | 262 °F | ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 122 °C | 252 °F | ASTM D648 |
Users viewing this material also viewed the following:
- Alcoa KAMA Petwich-PET 4300 Petwich-PET (discontinued **)
- Victrex® PEEK -HT™ 22GL30 Polyetherketone, 30% Glass Fiber Reinforced
- LATI Latamid 6 H2 G/30-V0CT1 PA 6, 30% Glass Fiber Reinforced, Heat Stabilized, Flame Retardant
- Samsung Cheil Industries Infino® NH-3402F PC, 40% Glass Filled FR
- Plenco 00714 Melamine-Phenolic, Granular, Injection Molded
- DSM Stanyl® TW363 Nylon 46 (European Grade) (Dry)
- CPC - Vycom CELTEC® Expanded Rigid foam PVC board
- DuPont Performance Polymers Zytel® 70G43HSLA BK099 Nylon 66 (Unverified Data**)
- Hippe PF WV 201 Wood veneer Reinforced Phenolic Resin - Sheet
Copyright © lookpolymers.com All Rights Reserved