- Polymer Property : Tensile Strength, Ultimate = 9570 psi
Polymer Property : Tensile Strength, Ultimate = 9570 psi Product List
Mechanical PropertiesTips: 30 items are displayed at most. For the rest of the results, please contact customer service.
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Ultimate | 66.0 MPa | 9570 psi | ASTM D638 |
| Plaskolite Optix® CA-61 General Purpose Acrylic Resin Injection Molding and Extrusion Grade Pellets. Good heat resistance, medium flow. |
|||
| Tensile Strength, Ultimate | 66.0 MPa | 9570 psi | 5 mm/min |
| Polimeri Europa KOSTIL B366 Styrene Acrylonitrile Symbol according to ISO 1043-1: SAN Grade designation according to ISO 4894-SAN 2,M,105-25 Injection moulding grade with good chemical resistance and easy flow grade Application fields: household.. |
|||
| Tensile Strength, Ultimate | 66.0 MPa | 9570 psi | ASTM D638 |
| Covestro Apec® DP9-9331 High-Heat Polycarbonate, General Purpose
(discontinued **) Information provided by Bayer Corporation, Plastics DivisionAs of 1 September 2015, Bayer MaterialScience was separated from Bayer AG and has officially adopted its new name – Covestro. This produ.. |
|||
| Tensile Strength, Ultimate | 66.0 MPa | 9570 psi | ASTM D638 |
| Covestro Apec® DP9-9333 High-Heat Polycarbonate, General Purpose, UV-Stabilized
(discontinued **) Information provided by Bayer Corporation, Plastics DivisionAs of 1 September 2015, Bayer MaterialScience was separated from Bayer AG and has officially adopted its new name – Covestro. This produ.. |
|||
| Tensile Strength, Ultimate | 66.0 MPa | 9570 psi | ASTM D638 |
| LG Chemical Lupoy 1300-22 Polycarbonate Resin Description: LUPOY PC 1300-22 resin is designed for extrusion and injection molding products. It exhibits an excellent physical property balance of heat resistance, transparency and impact strength... |
|||
| Tensile Strength, Ultimate | 66.0 MPa | 9570 psi | ASTM D638 |
| LG Chemical Lupoy 1301EP22 Polycarbonate Resin Description: LUPOY PC 1301EP-22 resin is designed for extrusion and injection molding products. It exhibits an excellent physical property balance of heat resistance, transparency and impact strengt.. |
|||
| Tensile Strength, Ultimate | 66.0 MPa | 9570 psi | ASTM D638 |
| LG Chemical Lupoy NF1005F 03R Polycarbonate Resin Description: LUPOY NF 1005F03R, eco-friendly UL94 V0/1.5 mm, is designed for extrusion products. It combines an excellent physical property balance of heat resistance, transparency and impact streng.. |
|||
| Tensile Strength, Ultimate | 66.0 MPa @Temperature 22.0 °C |
9570 psi @Temperature 71.6 °F |
25mm flat samples, compression moulded; ISO 527-4 |
| Menzolit Menzolit® SMC 0190 Unsaturated Polyester UP SMC 0190 is a general purpose SMC for applications in the field of electrical industry. Typical applications are housings, covers, wire distribution boxes and metering cabinets. The material meets t.. |
|||
| Tensile Strength, Ultimate | 66.0 MPa | 9570 psi | ASTM D638 |
| LG Chemical Lupoy 1201-22 Polycarbonate Resin Description: LUPOY PC 1201-22 resin is designed for extrusion and injection molding products. It exhibits an excellent physical property balance of heat resistance, transparency and impact strength... |
|||
| Tensile Strength, Ultimate | 66.0 MPa | 9570 psi | ASTM D638 |
| LG Chemical Lupoy 1201HP-21 Polycarbonate Resin Description: LUPOY PC 1201HP-21 resin is designed for extrusion and injection molding products. It exhibits an excellent physical property balance of heat resistance, transparency and impact strengt.. |
|||
| Tensile Strength, Ultimate | 66.0 MPa | 9570 psi | ASTM D638 |
| LG Chemical Lupoy 1201HP-22 Polycarbonate Resin Description: LUPOY PC 1201HP-22 resin is designed for extrusion and injection molding products. It exhibits an excellent physical property balance of heat resistance, transparency and impact strengt.. |
|||
| Tensile Strength, Ultimate | 66.0 MPa | 9570 psi | ASTM D638 |
| LG Chemical Lupoy 1302HP-21 Polycarbonate Resin Description: LUPOY PC 1302HP-21 resin is designed for extrusion and injection molding products. It exhibits an excellent physical property balance of heat resistance, transparency and impact strengt.. |
|||
| Tensile Strength, Ultimate | 66.0 MPa | 9570 psi | ASTM D638 |
| LG Chemical Lupoy 1302HP-22 Polycarbonate Resin Description: LUPOY PC 1302HP-22 resin is designed for extrusion and injection molding products. It exhibits an excellent physical property balance of heat resistance, transparency and impact strengt.. |
|||
| Tensile Strength, Ultimate | 66.0 MPa | 9570 psi | ASTM D638 |
| LyondellBasell Higlass SB224-3 Polypropylene Copolymer, 30% Glass Fiber Key Features: conventional melt flow, medium high modulus, chemically coupled, glass fiber-reinforced polypropylene copolymer, high impact strength, high stiffness, good processabilityApplications: .. |
|||
| Tensile Strength, Ultimate | 66.0 MPa | 9570 psi | ASTM Data |
| Dow Tyril® 990 SAN TYRIL® 990 SAN copolymer grade provides colorless glass-like clarity and excellent overall optical properties. It provides a profile of very good strength with stiffness, chemical resistance, heat .. |
|||
| Tensile Strength, Ultimate | 66.0 MPa | 9570 psi | ATSM D638 |
| Ashley Polymers Ashlene® 521/522 Nylon 66, TiO2 Filled General purpose grades of Nylon 66 containing 0.2% and 1.0% TiO2 respectively.Data provided by the manufacturer |
|||
| Tensile Strength, Ultimate | 66.0 MPa | 9570 psi | ASTM D638 |
| A. Schulman ComAlloy Comtuf® 523 Polycarbonate/Styrenic Alloy Data provided by the manufacturer, ComAlloy International Company. Superior toughness and impact resistance characterize Comtuf® materialsThe ComAlloy product line has been integrated into the A Sc.. |
|||
| Tensile Strength, Ultimate | 66.0 MPa | 9570 psi | ASTM D638 |
| A. Schulman ComAlloy Hiloy® 247 SAN, Glass/Mineral Reinforced, UL Data provided by the manufacturer, ComAlloy International Company.40% Glass/Mineral Reinforced.The ComAlloy product line has been integrated into the A Schulman product line. |
|||
| Tensile Strength, Ultimate | 66.0 MPa | 9570 psi | ASTM D638 |
| A. Schulman ComAlloy Lubrilon® 512 Polycarbonate, Glass Fiber/PTFE, UL Data provided by the manufacturer, ComAlloy International Company. High performance and excellent lubricity with minimal surface wear.The ComAlloy product line has been integrated into the A Schulma.. |
|||
| Tensile Strength, Ultimate | 66.0 MPa | 9570 psi | ATSM D638 |
| Ashley Polymers Ashlene® 1041R Polycarbonate A general purpose, injection molding grade, natural resin.Data provided by the manufacturer |
|||
| Tensile Strength, Ultimate | 66.0 MPa | 9570 psi | ATSM D638 |
| Ashley Polymers Ashlene® 735LD Nylon 6 An impact modified, plasticized copolymer with improved impact resistance for injection molding.Data provided by the manufacturer |
|||
| Tensile Strength, Ultimate | 66.0 MPa | 9570 psi | ATSM D638 |
| Ashley Polymers Ashlene® 736LD Nylon 6 Modified to retain toughness at low temperatures for injection molding.Data provided by the manufacturer |
|||
| Tensile Strength, Ultimate | 66.0 MPa | 9570 psi | ATSM D638 |
| Ashley Polymers Ashlene® 935 Nylon 11 An unplasticized Nylon 11 for extrusion applications.Data provided by the manufacturer |
|||
| Tensile Strength, Ultimate | 66.0 MPa | 9570 psi | ASTM D638 |
| A. Schulman ComAlloy Voloy® 681 Nylon 6/6, Glass Fiber/Bead Reinforced, Nylon 6/6 Alloy, Flame Retardant, UL Data provided by the manufacturer, ComAlloy International Company.45% Glass Fiber/Bead Reinforced. Halogen- and phosphorous-freeThe ComAlloy product line has been integrated into the A Schulman prod.. |
|||
| Tensile Strength, Ultimate | 66.0 MPa | 9570 psi | ASTM D638 |
| Plaskolite West Optix® CA-61 General Purpose Acrylic Resin Injection Molding and Extrusion Grade Pellets. Good heat resistance, medium flow. |
|||
| Tensile Strength, Ultimate | 66.0 MPa | 9570 psi | XY; ASTM D638 |
| ALM PA 601-CF Filled Nylon 12 Prototyping Polymer Carbon fiber filled nylon 12 easy to process, strong light weight filled material.Low density, good dimensional stability while maintaining excellent mechanical properties.Fibers have been optimized.. |
|||
| Tensile Strength, Ultimate | 66.0 MPa | 9570 psi | ASTM D638 |
| PolyOne Edgetek® MP-1000 Modified PPO - Unreinforced
(discontinued **) Data provided by PolyOne. |
|||
| Tensile Strength, Ultimate | 66.0 MPa | 9570 psi | ISO 527 |
| LATI LARIL 13 Light Brown Polyphenylene Oxide (PPOm)
(discontinued **) Description: Laril thermoplastics are polyphenylene oxide (PPOm) products. They exhibit excellent toughness, even at low temperatures, good thermal resistance and dimensional stability are the most .. |
|||
| Tensile Strength, Ultimate | 66.0 MPa | 9570 psi | ISO 527-1, 2 |
| Polyplastics Duracon® CP-15X Acetal Co-polymer (POM), Creep resistant, Creep resistant DURACON® is a crystalline thermoplastic acetal copolymer. The primary raw material trioxane, a trimer of formaldehyde.The thermoplastic adopts a copolymer structure in which polyoxymethylene (-C-O).. |
|||
| Tensile Strength, Ultimate | 66.0 MPa | 9570 psi | ATSM D638 |
| Ashley Polymers Ashlene® P1021R Polycarbonate A prime general purpose injection molding grade, natural resin with easy mold release.Data provided by the manufacturer |
|||