Ashley Polymers Ashlene® 195-N2 Acetal
| Category | Polymer , Thermoplastic , Acetal (POM) , Acetal Copolymer, Unreinforced |
| Manufacturer | Ashley Polymers |
| Trade Name | Ashlene® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Ashley Polymers Ashlene® 195-N2 Acetal.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
A general purpose, medium viscosity natural.Data provided by the manufacturer
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.41 g/cc | 0.0509 lb/in³ | ASTM D792 |
| Water Absorption | 0.22 % | 0.22 % | ASTM D570 |
| Linear Mold Shrinkage | 0.022 cm/cm | 0.022 in/in | ASTM D955 |
| Melt Flow | 27 g/10 min | 27 g/10 min |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell M | 80 | 80 | ASTM D785 |
| Tensile Strength, Ultimate | 62.0 MPa | 8990 psi | ATSM D638 |
| Elongation at Break | 50 % | 50 % | ASTM D638 |
| Flexural Strength | 91.0 MPa | 13200 psi | ASTM D790 |
| Flexural Modulus | 2.60 GPa | 377 ksi | ASTM D790 |
| Shear Strength | 55.0 MPa | 7980 psi | ASTM D732 |
| Izod Impact, Notched | 0.540 J/cm | 1.01 ft-lb/in | ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Melting Point | 165 °C | 329 °F | ASTM D3418 |
| Deflection Temperature at 0.46 MPa (66 psi) | 158 °C | 316 °F | ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 110 °C | 230 °F | ASTM D648 |
| Flammability, UL94 | HB @Thickness 0.800 mm |
HB @Thickness 0.0315 in |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Dielectric Constant | 3.7 @Frequency 1e+6 Hz |
3.7 @Frequency 1e+6 Hz |
ASTM D150 |
| Dissipation Factor | 0.0070 @Frequency 1e+6 Hz |
0.0070 @Frequency 1e+6 Hz |
ASTM D150 |
Users viewing this material also viewed the following:
- Plastcom SLOVAMID 66 MI PA66, improved strength
- Kinlead PG14 Bag Grade BOPP Plain Film (thickness: 25 µm)
- LG Chemical NBR 3280 High Acrylonitrile Polymer
- Lucent Polymers PC-1418 Polycarbonate, Injection Grade
- Lucite International Elvacite ® 2014 Acrylic Resin
- Solvay Specialty Polymers Amodel® AS-4133 L Polyphthalamide (PPA), 33% Glass Fiber (Conditioned)
- Toho Tenax Besfight® MC Type II (6000 Filament) Nickel Coated Carbon Fiber
- Tra-Con Tra-Bond Ablebond 724-1 Polyurethane Adhesive
- Goodfellow Titanium Bronze
- Plenco 6527 Phenolic, Granular, Injection Molded
Copyright © lookpolymers.com All Rights Reserved