Ascend Performance Materials Vydyne® 49 Nylon 66, Conditioned

Category	Polymer , Thermoplastic , Nylon , Nylon 66
Manufacturer	Ascend Performance Materials (formerly Solutia)
Trade Name	VYDYNE®
Port	Ningbo port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	Ascend Performance Materials Vydyne® 49 Nylon 66, Conditioned.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

Vydyne® 49 is a general-purpose, impact-modified PA66 resin. Available in natural, it is recognized for all the processing and property advantages inherent to PA66 with the addition of improved impact strength. This resin offers a well balanced combination of engineering properties characterized by high melt point, good surface lubricity, abrasion resistance and resistance to many chemicals, machine and motor oils, solvents and gasoline.Availability:Asia PacificEuropeNorth America Additive:Impact Modifier Features:Gasoline ResistanceGeneral PurposeGood Abrasion ResistanceGood Chemical ResistanceGood ProcessabilityGood ToughnessHigh Impact ResistanceImpact ModifiedLow Temperature Impact ResistanceOil ResistantSolvent ResistantUses: Automotive ApplicationsConnectorsConsumer ApplicationsElectrical/Electronic ApplicationsFastenersGears General PurposeIndustrial ApplicationsAppearance: Natural ColorForms: PelletsProcessing Method: Injection MoldingInformation provided by Ascend

Physical Properties	Metric	English	Comments
Specific Gravity	1.11 g/cc	1.11 g/cc	ISO 1183
Water Absorption	1.3 %	1.3 %	24 hrs; ISO 62
Moisture Absorption at Equilibrium	2.3 %	2.3 %	50% RH; ISO 62
Linear Mold Shrinkage	0.018 cm/cm @Thickness 2.00 mm	0.018 in/in @Thickness 0.0787 in	ISO 294-4
Linear Mold Shrinkage, Transverse	0.016 cm/cm @Thickness 2.00 mm	0.016 in/in @Thickness 0.0787 in	ISO 294-4

Mechanical Properties	Metric	English	Comments
Tensile Strength at Break	42.0 MPa	6090 psi	ISO 527
Tensile Strength, Yield	50.0 MPa	7250 psi	ISO 527
Elongation at Break	40 %	40 %	ISO 527
Tensile Modulus	21.3 GPa	3090 ksi	ISO 527-2
Flexural Strength	27.0 MPa	3920 psi	ISO 178
Flexural Modulus	0.890 GPa	129 ksi	ISO 178
Izod Impact, Notched (ISO)	10.0 kJ/m² @Temperature -40.0 °C	4.76 ft-lb/in² @Temperature -40.0 °F	ISO 180
	15.0 kJ/m² @Temperature -30.0 °C	7.14 ft-lb/in² @Temperature -22.0 °F	ISO 180
	37.0 kJ/m² @Temperature 23.0 °C	17.6 ft-lb/in² @Temperature 73.4 °F	ISO 180
Charpy Impact Unnotched	NB @Temperature -30.0 °C	NB @Temperature -22.0 °F	ISO 179
	NB @Temperature 23.0 °C	NB @Temperature 73.4 °F	ISO 179
Charpy Impact, Notched	0.600 J/cm² @Temperature -40.0 °C	2.86 ft-lb/in² @Temperature -40.0 °F	ISO 179
	1.00 J/cm² @Temperature -30.0 °C	4.76 ft-lb/in² @Temperature -22.0 °F	ISO 179
	4.30 J/cm² @Temperature 23.0 °C	20.5 ft-lb/in² @Temperature 73.4 °F	ISO 179