- Ascend Performance Materials VYDYNE® R513 Nylon, 13% Glass Reinforced
Ascend Performance Materials VYDYNE® R513 Nylon, 13% Glass Reinforced
| Category | Polymer , Thermoplastic , Nylon , Nylon 66 , Nylon 66, 10% Glass Fiber Filled |
| Manufacturer | Ascend Performance Materials (formerly Solutia) |
| Trade Name | VYDYNE® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Ascend Performance Materials VYDYNE® R513 Nylon, 13% Glass Reinforced.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Typical property data. VYDYNE is a registered trademark of Solutia Inc.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.22 g/cc | 0.0441 lb/in³ | ASTM D792 |
| Water Absorption | 1.0 % | 1.0 % | 24 hours; ASTM D570 |
| Moisture Absorption at Equilibrium | 2.2 % | 2.2 % | ASTM D570 |
| Water Absorption at Saturation | 7.1 % | 7.1 % | ASTM D570 |
| Linear Mold Shrinkage | 0.0040 - 0.0080 cm/cm | 0.0040 - 0.0080 in/in | ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell M | 95 | 95 | ASTM D785 |
| Tensile Strength, Ultimate | 124 MPa | 18000 psi | ASTM D638 |
| Elongation at Break | 3.0 % | 3.0 % | ASTM D638 |
| Flexural Yield Strength | 179 MPa | 26000 psi | ASTM D790 |
| Flexural Modulus | 5.50 GPa | 798 ksi | ASTM D790 |
| Compressive Yield Strength | 172 MPa | 24900 psi | at 1% deformation; ASTM D695 |
| Shear Strength | 76.0 MPa | 11000 psi | ASTM D732 |
| Izod Impact, Notched | 0.500 J/cm @Thickness 3.17 mm |
0.937 ft-lb/in @Thickness 0.125 in |
ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 27.0 µm/m-°C @Temperature -40.0 - 82.0 °C |
15.0 µin/in-°F @Temperature -40.0 - 180 °F |
|
| Melting Point | 260 °C | 500 °F | ASTM D1525 |
| Deflection Temperature at 1.8 MPa (264 psi) | 245 °C @Thickness 3.17 mm |
473 °F @Thickness 0.125 in |
Unannealed; ASTM D648 |
| Flammability, UL94 | HB | HB | |
| Oxygen Index | 25 % | 25 % | ASTM D2863 |
Users viewing this material also viewed the following:
- MV Labs HG400 HgCl2 Mercury(II) chloride
- Mar-Bal MB3000-20NY Thermoset Polyester Composite Molding Compound
- H.C. Starck Pure Molybdenum GME Glass Melting Electrodes
- Lehmann & Voss LUVOCOM® 1105-8001 PEEK, with glass spheres
- SMAC SMACMOUNT® 2528S 03 Damping Material
- A. Schulman POLYBATCH™ White P8555 SC Concentrate Based In Random Copolymer Polypropylene
- A. Schulman POLYBATCH™ Gold 7060E POLYBATCH® Concentrate Based In LDPE
- EMS-Grivory Grivory® TSC-20/4 EC black 9832 PA666-CF20
- 3M Scotch-Weld™ DP8010NS Structural Adhesive
- DuPont Performance Polymers Minlon® IG38C1 BK434 Nylon 66 (Unverified Data**)
Copyright © lookpolymers.com All Rights Reserved