Lubrizol ESTALOC® T514 Ester-Type, Reinforced Engineering Thermoplastic (European Grade)

Category	Polymer , Thermoplastic , Elastomer, TPE , Polyurethane, TP , Thermoplastic Polyurethane, Elastomer, Glass Filled
Manufacturer	Lubrizol (former Noveon)
Trade Name	ESTALOC®
Port	Ningbo port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	Lubrizol ESTALOC® T514 Ester-Type, Reinforced Engineering Thermoplastic (European Grade).pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

Description: Estaloc® RETP (Reinforced Engineering Thermoplastic) is a tough, dimensionally stable, abrasion-resistant thermoplastic that withstands demanding environments. Developed as an extension to the Noveon Estane® TPU technology, Estaloc® RETP products complement Estane's durability and aesthetics with increased stiffness capability and dimensional stability over a broad temperature performance range not available from other engineering thermoplastics.Major Benefits of Estaloc® RETPs: Superior Dimensional Stability approaching that of metalsClass A surface aestheticsPaintability with no primer nor adhesion promoterExcellent abrasion and scuff/mar resistanceToughness over a broad temperature rangeExcellent adhesion to a variety of overmolding chemistriesInformation provided by Noveon, Inc.

Physical Properties	Metric	English	Comments
Specific Gravity	1.35 g/cc	1.35 g/cc	ISO 1183
Filler Content	18 %	18 %
Linear Mold Shrinkage	0.0020 cm/cm	0.0020 in/in	ASTM D955

Mechanical Properties	Metric	English	Comments
Hardness, Shore D	72	72	ISO 868
Tensile Strength, Ultimate	59.0 MPa	8560 psi	ISO 527-2/1A/5
Elongation at Break	19 %	19 %	ISO 527-2/1A/5
Tensile Modulus	2.37 GPa	344 ksi	ISO 527-2/1A/1
Flexural Strength	69.0 MPa	10000 psi	ISO 178
Flexural Modulus	2.20 GPa	319 ksi	ISO 178
Izod Impact, Notched (ISO)	13.0 kJ/m²	6.19 ft-lb/in²	Low Temp; ISO 180/1eA
	45.0 kJ/m²	21.4 ft-lb/in²	ISO 180/1eA
Izod Impact, Unnotched (ISO)	105 kJ/m²	50.0 ft-lb/in²	ISO 180/1eU
	52.0 kJ/m² @Temperature -30.0 °C	24.7 ft-lb/in² @Temperature -22.0 °F	ISO 180/1eU
Charpy Impact Unnotched	11.3 J/cm²	53.8 ft-lb/in²	ISO 179/1eU
	45.0 J/cm² @Temperature -30.0 °C	214 ft-lb/in² @Temperature -22.0 °F	ISO 179/1eU
Charpy Impact, Notched	4.70 J/cm²	22.4 ft-lb/in²	ISO 179/1eA
	1.20 J/cm² @Temperature -30.0 °C	5.71 ft-lb/in² @Temperature -22.0 °F	ISO 179/1eA
Taber Abrasion, mg/1000 Cycles	10	10	CS-17 wheel; ASTM D1044

Thermal Properties	Metric	English	Comments
CTE, linear	28.3 µm/m-°C @Temperature 20.0 °C	15.7 µin/in-°F @Temperature 68.0 °F	ASTM D696
Deflection Temperature at 0.46 MPa (66 psi)	199 °C	390 °F	method Bf; ISO 75-2
Deflection Temperature at 1.8 MPa (264 psi)	135 °C	275 °F	method Af; ISO 75-2
Vicat Softening Point	117 °C	243 °F	temperature B; ISO 36
	182 °C	360 °F	temperature A; ISO 306