Abatron AboCast/AboCure 8109-13

Category Polymer , Adhesive , Thermoset , Epoxy
Manufacturer Abatron
Trade Name AboCast/AboCure
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Abatron AboCast/AboCure 8109-13.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Liquid hardener version of AboCast/AboCure 8109-11.Processing: 100/23 pbw; Potlife: 3-5 h/20°C (68°F), 1-3 h/40°C (105°F), 0.5-1 h/60°C (140°F); mix at RT; cures in: 30 mins/60°C (140°F), 45 min/100°C (212°F), 30 mins/140°C (285°F), 15 min+1-3h/180°C (355°F).Applications: Potting and laminating.
Physical Properties Metric English Comments
Density 1.18 g/cc
0.0426 lb/in³
Water Absorption 0.30 - 0.40 %
0.30 - 0.40 %
(60x10X4 mm bar) after 1 hour at 100°C (212°F)
0.40 - 0.50 %
0.40 - 0.50 %
(60x10X4 mm bar) after 10 days at 20°C (77°F)
Viscosity 1000 - 2000 cP

@Temperature 40.0 °C
1000 - 2000 cP

@Temperature 104 °F
10000 - 15000 cP

@Temperature 21.0 °C
10000 - 15000 cP

@Temperature 69.8 °F
Mechanical Properties Metric English Comments
Tensile Strength, Ultimate 68.95 MPa
10000 psi
Modulus of Elasticity 3.447 GPa
500.0 ksi
Flexural Yield Strength 137.9 MPa
20000 psi
Compressive Yield Strength 151.7 MPa
22000 psi
Thermal Properties Metric English Comments
CTE, linear 50.0 - 55.0 µm/m-°C

@Temperature 20.0 °C
27.8 - 30.6 µin/in-°F

@Temperature 68.0 °F
Maximum Service Temperature, Air 150 °C
302 °F
Deflection temperature; load unknown.
Electrical Properties Metric English Comments
Electrical Resistivity >= 1.50e+16 ohm-cm
>= 1.50e+16 ohm-cm
Dielectric Constant 3.9 - 4.4

@Frequency 1e+6 Hz
3.9 - 4.4

@Frequency 1e+6 Hz
4.2 - 4.5

@Frequency 50 Hz
4.2 - 4.5

@Frequency 50 Hz
Dielectric Strength 15.7 - 17.7 kV/mm

@Thickness 3.17 mm
400 - 450 kV/in

@Thickness 0.125 in
Short time value
Processing Properties Metric English Comments
Processing Temperature 25.0 °C
77.0 °F
Pot Life 30.0 - 60.0 min

@Temperature 60.0 °C
30.0 - 60.0 min

@Temperature 140 °F
60.0 - 180 min

@Temperature 40.0 °C
60.0 - 180 min

@Temperature 104 °F
180 - 300 min

@Temperature 20.0 °C
180 - 300 min

@Temperature 68.0 °F