DuPont Performance Polymers Hytrel® DYM350BK TPC-ET+PBT  (Unverified Data**)

Category Polymer , Thermoplastic , Polyester, TP , Polybutylene Terephthalate (PBT) , Polyester Thermoplastic Elastomer
Manufacturer DuPont Performance Polymers
Trade Name Hytrel®
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF DuPont Performance Polymers Hytrel® DYM350BK TPC-ET+PBT  (Unverified Data**).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Medium Modulus Polyester Elastomer with Excellent Impact Resistance Developed for Air Bag Door ApplicationsInformation provided by DuPont Performance Polymers
Physical Properties Metric English Comments
Density 1.00 g/cc
0.0361 lb/in³
1.18 g/cc
0.0426 lb/in³
ISO 1183
Water Absorption 0.60 %

@Thickness 2.00 mm
 0.60 %

@Thickness 0.0787 in
 Sim. to ISO 62
Moisture Absorption 0.200 %

@Thickness 2.00 mm
 0.200 %

@Thickness 0.0787 in
 Sim. to ISO 62
Water Absorption at Saturation 0.60 %
0.60 %
Immersion 24h; ASTM D570
Linear Mold Shrinkage, Flow 0.013 cm/cm
0.013 in/in
ISO 294-4 2577
Linear Mold Shrinkage, Transverse 0.014 cm/cm
0.014 in/in
ISO 294-4 2577
Melt Flow 14 g/10 min

@Load 2.16 kg,
Temperature 240 °C
 14 g/10 min

@Load 4.76 lb,
Temperature 464 °F
 cm³/10min; ISO 1133
15 g/10 min

@Load 2.16 kg,
Temperature 240 °C
 15 g/10 min

@Load 4.76 lb,
Temperature 464 °F
 ISO 1133
Mechanical Properties Metric English Comments
Hardness, Shore D 50
50
15s; ISO 868
<= 55
<= 55
ISO 868
Tensile Strength at Break 35.0 MPa
5080 psi
ISO 527-1/-2
Tensile Stress 10.5 MPa

@Strain 5.00 %
 1520 psi

@Strain 5.00 %
 ISO 527-1/-2
13.0 MPa

@Strain 10.0 %
 1890 psi

@Strain 10.0 %
 ISO 527-1/-2
16.0 MPa

@Strain 50.0 %
 2320 psi

@Strain 50.0 %
 ISO 527-1/-2
3.65 MPa

@Strain 7.23 %,
Temperature 120 °C
 529 psi

@Strain 7.23 %,
Temperature 248 °F
 TPE; ISO 11403-1 -2
3.94 MPa

@Strain 5.00 %,
Temperature 80.0 °C
 571 psi

@Strain 5.00 %,
Temperature 176 °F
 TPE; ISO 11403-1 -2
4.64 MPa

@Strain 7.63 %,
Temperature 100 °C
 673 psi

@Strain 7.63 %,
Temperature 212 °F
 TPE; ISO 11403-1 -2
5.13 MPa

@Strain 7.75 %,
Temperature 90.0 °C
 744 psi

@Strain 7.75 %,
Temperature 194 °F
 TPE; ISO 11403-1 -2
5.38 MPa

@Strain 18.24 %,
Temperature 120 °C
 780 psi

@Strain 18.24 %,
Temperature 248 °F
 TPE; ISO 11403-1 -2
5.92 MPa

@Strain 28.56 %,
Temperature 120 °C
 859 psi

@Strain 28.56 %,
Temperature 248 °F
 TPE; ISO 11403-1 -2
6.17 MPa

@Strain 38.88 %,
Temperature 120 °C
 895 psi

@Strain 38.88 %,
Temperature 248 °F
 TPE; ISO 11403-1 -2
6.32 MPa

@Strain 49.89 %,
Temperature 120 °C
 917 psi

@Strain 49.89 %,
Temperature 248 °F
 TPE; ISO 11403-1 -2
6.46 MPa

@Strain 63.66 %,
Temperature 120 °C
 937 psi

@Strain 63.66 %,
Temperature 248 °F
 TPE; ISO 11403-1 -2
6.61 MPa

@Strain 78.11 %,
Temperature 120 °C
 959 psi

@Strain 78.11 %,
Temperature 248 °F
 TPE; ISO 11403-1 -2
6.66 MPa

@Strain 18.26 %,
Temperature 100 °C
 966 psi

@Strain 18.26 %,
Temperature 212 °F
 TPE; ISO 11403-1 -2
6.75 MPa

@Strain 91.87 %,
Temperature 120 °C
 979 psi

@Strain 91.87 %,
Temperature 248 °F
 TPE; ISO 11403-1 -2
6.92 MPa

@Strain 106.32 %,
Temperature 120 °C
 1000 psi

@Strain 106.32 %,
Temperature 248 °F
 TPE; ISO 11403-1 -2
7.19 MPa

@Strain 127.66 %,
Temperature 120 °C
 1040 psi

@Strain 127.66 %,
Temperature 248 °F
 TPE; ISO 11403-1 -2
7.30 MPa

@Strain 15.0 %,
Temperature 80.0 °C
 1060 psi

@Strain 15.0 %,
Temperature 176 °F
 TPE; ISO 11403-1 -2
7.32 MPa

@Strain 28.88 %,
Temperature 100 °C
 1060 psi

@Strain 28.88 %,
Temperature 212 °F
 TPE; ISO 11403-1 -2
7.37 MPa

@Strain 18.54 %,
Temperature 90.0 °C
 1070 psi

@Strain 18.54 %,
Temperature 194 °F
 TPE; ISO 11403-1 -2
7.38 MPa

@Strain 7.86 %,
Temperature 60.0 °C
 1070 psi

@Strain 7.86 %,
Temperature 140 °F
 TPE; ISO 11403-1 -2
7.41 MPa

@Strain 141.42 %,
Temperature 120 °C
 1070 psi

@Strain 141.42 %,
Temperature 248 °F
 TPE; ISO 11403-1 -2
7.61 MPa

@Strain 40.16 %,
Temperature 100 °C
 1100 psi

@Strain 40.16 %,
Temperature 212 °F
 TPE; ISO 11403-1 -2
7.71 MPa

@Strain 159.31 %,
Temperature 120 °C
 1120 psi

@Strain 159.31 %,
Temperature 248 °F
 TPE; ISO 11403-1 -2
7.77 MPa

@Strain 50.78 %,
Temperature 100 °C
 1130 psi

@Strain 50.78 %,
Temperature 212 °F
 TPE; ISO 11403-1 -2
7.93 MPa

@Strain 65.39 %,
Temperature 100 °C
 1150 psi

@Strain 65.39 %,
Temperature 212 °F
 TPE; ISO 11403-1 -2
8.07 MPa

@Strain 29.33 %,
Temperature 90.0 °C
 1170 psi

@Strain 29.33 %,
Temperature 194 °F
 TPE; ISO 11403-1 -2
8.09 MPa

@Strain 79.33 %,
Temperature 100 °C
 1170 psi

@Strain 79.33 %,
Temperature 212 °F
 TPE; ISO 11403-1 -2
8.21 MPa

@Strain 184.09 %,
Temperature 120 °C
 1190 psi

@Strain 184.09 %,
Temperature 248 °F
 TPE; ISO 11403-1 -2
8.26 MPa

@Strain 93.93 %,
Temperature 100 °C
 1200 psi

@Strain 93.93 %,
Temperature 212 °F
 TPE; ISO 11403-1 -2
8.36 MPa

@Strain 40.11 %,
Temperature 90.0 °C
 1210 psi

@Strain 40.11 %,
Temperature 194 °F
 TPE; ISO 11403-1 -2
8.45 MPa

@Strain 108.54 %,
Temperature 100 °C
 1230 psi

@Strain 108.54 %,
Temperature 212 °F
 TPE; ISO 11403-1 -2
8.50 MPa

@Strain 5.00 %,
Temperature 23.0 °C
 1230 psi

@Strain 5.00 %,
Temperature 73.4 °F
 ISO 11403-1 -2
8.53 MPa

@Strain 50.9 %,
Temperature 90.0 °C
 1240 psi

@Strain 50.9 %,
Temperature 194 °F
 TPE; ISO 11403-1 -2
8.64 MPa

@Strain 30.0 %,
Temperature 80.0 °C
 1250 psi

@Strain 30.0 %,
Temperature 176 °F
 TPE; ISO 11403-1 -2
8.64 MPa

@Strain 5.00 %,
Temperature 0.000 °C
 1250 psi

@Strain 5.00 %,
Temperature 32.0 °F
 ISO 11403-1 -2
8.70 MPa

@Strain 65.06 %,
Temperature 90.0 °C
 1260 psi

@Strain 65.06 %,
Temperature 194 °F
 TPE; ISO 11403-1 -2
8.76 MPa

@Strain 129.78 %,
Temperature 100 °C
 1270 psi

@Strain 129.78 %,
Temperature 212 °F
 TPE; ISO 11403-1 -2
8.86 MPa

@Strain 212.3 %,
Temperature 120 °C
 1290 psi

@Strain 212.3 %,
Temperature 248 °F
 TPE; ISO 11403-1 -2
8.86 MPa

@Strain 79.22 %,
Temperature 90.0 °C
 1290 psi

@Strain 79.22 %,
Temperature 194 °F
 TPE; ISO 11403-1 -2
9.01 MPa

@Strain 144.39 %,
Temperature 100 °C
 1310 psi

@Strain 144.39 %,
Temperature 212 °F
 TPE; ISO 11403-1 -2
9.07 MPa

@Strain 94.05 %,
Temperature 90.0 °C
 1320 psi

@Strain 94.05 %,
Temperature 194 °F
 TPE; ISO 11403-1 -2
9.20 MPa

@Strain 45.0 %,
Temperature 80.0 °C
 1330 psi

@Strain 45.0 %,
Temperature 176 °F
 TPE; ISO 11403-1 -2
9.24 MPa

@Strain 108.21 %,
Temperature 90.0 °C
 1340 psi

@Strain 108.21 %,
Temperature 194 °F
 TPE; ISO 11403-1 -2
9.36 MPa

@Strain 162.31 %,
Temperature 100 °C
 1360 psi

@Strain 162.31 %,
Temperature 212 °F
 TPE; ISO 11403-1 -2
9.57 MPa

@Strain 8.12 %,
Temperature 40.0 °C
 1390 psi

@Strain 8.12 %,
Temperature 104 °F
 TPE; ISO 11403-1 -2
9.59 MPa

@Strain 129.78 %,
Temperature 90.0 °C
 1390 psi

@Strain 129.78 %,
Temperature 194 °F
 TPE; ISO 11403-1 -2
9.73 MPa

@Strain 247.4 %,
Temperature 120 °C
 1410 psi

@Strain 247.4 %,
Temperature 248 °F
 TPE; ISO 11403-1 -2
9.85 MPa

@Strain 144.61 %,
Temperature 90.0 °C
 1430 psi

@Strain 144.61 %,
Temperature 194 °F
 TPE; ISO 11403-1 -2
9.91 MPa

@Strain 187.53 %,
Temperature 100 °C
 1440 psi

@Strain 187.53 %,
Temperature 212 °F
 TPE; ISO 11403-1 -2
10.12 MPa

@Strain 18.8 %,
Temperature 60.0 °C
 1468 psi

@Strain 18.8 %,
Temperature 140 °F
 TPE; ISO 11403-1 -2
10.19 MPa

@Strain 162.14 %,
Temperature 90.0 °C
 1478 psi

@Strain 162.14 %,
Temperature 194 °F
 TPE; ISO 11403-1 -2
10.61 MPa

@Strain 216.08 %,
Temperature 100 °C
 1539 psi

@Strain 216.08 %,
Temperature 212 °F
 TPE; ISO 11403-1 -2
10.76 MPa

@Strain 187.76 %,
Temperature 90.0 °C
 1561 psi

@Strain 187.76 %,
Temperature 194 °F
 TPE; ISO 11403-1 -2
Users viewing this material also viewed the following: