Premix Premi-Glas® 3140-22 Fiberglass Reinforced Thermoset Thick Molding Compound

Category	Polymer , Thermoset , Filled/Reinforced Thermoset
Manufacturer	Premix
Trade Name	Premi-Glas®
Port	Shanghai port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	Premix Premi-Glas® 3140-22 Fiberglass Reinforced Thermoset Thick Molding Compound.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

Premi-Glas® 3140-22 is a fiberglass reinforced thermoset thick molding compound for electrical and flame retardant applications.Key features and benefits are:TMC compounding process preserves glass integrity for strength vs. BMCGood dimensional stability, including excellent thermal resistancePigmentable for molded-in color; best appearance with mold textureRecognized by Underwriter's Laboratories, File #E42524Designed for injection or compression molding in matched metal die molds.Information provided by Premix.

Physical Properties	Metric	English	Comments
Specific Gravity	1.75 - 1.85 g/cc	1.75 - 1.85 g/cc
Linear Mold Shrinkage	0.0015 - 0.0025 cm/cm	0.0015 - 0.0025 in/in	Polymerization Shrinkage

Mechanical Properties	Metric	English	Comments
Tensile Strength	56.0 MPa	8120 psi	ASTM D638
Tensile Modulus	10.0 GPa	1450 ksi	ASTM D638
Flexural Strength	135 MPa	19600 psi	ASTM D790
Flexural Modulus	9.00 GPa	1310 ksi	ASTM D790
Poissons Ratio	0.30	0.30
Shear Modulus	3.80 GPa	551 ksi	Calculated
Izod Impact, Notched	7.00 J/cm	13.1 ft-lb/in	ASTM D256
Izod Impact, Unnotched	9.00 J/cm	16.9 ft-lb/in	ASTM D4812

Thermal Properties	Metric	English	Comments
CTE, linear, Parallel to Flow	35.0 µm/m-°C	19.4 µin/in-°F	Z Direction
CTE, linear, Transverse to Flow	25.0 µm/m-°C	13.9 µin/in-°F	XY Direction
Thermal Conductivity	0.300 W/m-K	2.08 BTU-in/hr-ft²-°F
UL RTI, Electrical	130 °C	266 °F	UL 746C
UL RTI, Mechanical with Impact	130 °C	266 °F	UL 746C
UL RTI, Mechanical without Impact	130 °C	266 °F	UL 746C
Flammability, UL94	V-0 @Thickness 1.50 mm	V-0 @Thickness 0.0591 in

Electrical Properties	Metric	English	Comments
Dielectric Strength	15.0 kV/mm	381 kV/in	ASTM D149
Arc Resistance	>= 180 sec	>= 180 sec	ASTM D495
Comparative Tracking Index	600 V	600 V	ASTM D2303

Processing Properties	Metric	English	Comments
Processing Temperature	150 °C	302 °F	Injection or Compression Molding
Clamp Pressure	3.45 - 6.89 MPa	500 - 1000 psi	Molding Pressure