- Asahi Kasei Leona® 90G33 33% Glass Filled Nylon 66
Asahi Kasei Leona® 90G33 33% Glass Filled Nylon 66
| Category | Polymer , Thermoplastic , Nylon , Nylon 66 , Nylon 66, 30% Glass Fiber Filled |
| Manufacturer | Asahi Kasei |
| Trade Name | Leona® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Asahi Kasei Leona® 90G33 33% Glass Filled Nylon 66.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Enhanced strength and stiffness; with 33% GF. Superior fluidity and appearance.Applications:Automotive parts Information provided by Asahi Kasei
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.39 g/cc | 1.39 g/cc | Dry; ASTM D792 |
| Water Absorption | 1.4 % | 1.4 % | Wet |
| Linear Mold Shrinkage | 0.0040 cm/cm | 0.0040 in/in | Dry; ASTM D2863 |
| Linear Mold Shrinkage, Transverse | 0.0090 cm/cm | 0.0090 in/in | Dry; ASTM D2863 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell M | 90 | 90 | Dry; ASTM D785 |
| Hardness, Rockwell R | 120 | 120 | Dry; ASTM D785 |
| Tensile Strength, Yield | 157 MPa | 22800 psi | Wet; ASTM D638 |
| 194 MPa | 28100 psi | Dry; ASTM D638 | |
| Elongation at Break | 3.0 % | 3.0 % | Dry; ASTM D638 |
| 4.0 % | 4.0 % | Wet; ASTM D638 | |
| Flexural Strength | 245 MPa | 35500 psi | Wet; ASTM D790 |
| 294 MPa | 42600 psi | Dry; ASTM D790 | |
| Flexural Modulus | 7.60 GPa | 1100 ksi | Wet; ASTM D790 |
| 9.60 GPa | 1390 ksi | Dry; ASTM D790 | |
| Izod Impact, Notched | 0.980 J/cm | 1.84 ft-lb/in | Dry; ASTM D256 |
| 1.18 J/cm | 2.21 ft-lb/in | Wet; ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 30.0 µm/m-°C @Temperature 20.0 °C |
16.7 µin/in-°F @Temperature 68.0 °F |
Dry; ASTM D696 |
| Deflection Temperature at 1.8 MPa (264 psi) | 220 °C | 428 °F | Dry; ASTM D648 |
Users viewing this material also viewed the following:
- GRECO ISOTHANE 5090A Polyether TPU Resin
- LATI Latamid 66 H2PX-V0 PA 66, Heat Stabilized, Flame Retardant
- Techmer ES HiFill® PP GF15 CC 15% Glass Filled
- Struktol POLYDIS 3693 Elastomer modified epoxy prepolymer
- A. Schulman FORMION™ FI 200 Non-Reinforced, Injection Molding Grade Ionomer / Nylon Alloy
- A. Schulman POLYBATCH™ House Red 50311U/4 Concentrate Based In LLDPE
- Diamond Polymers DIAMALOY 1001 CF40 40% Carbon Fiber Filled ABS
- Asahi Glass Fluon® C-88AXP ETFE Fluororesin
- NOVA Chemicals Novapol® TR-0535-UG Hexene MDPE Rotational Molding Resin (discontinued **)
- BASF 2-Pyrrolidone Distilled
Copyright © lookpolymers.com All Rights Reserved