Category | Polymer , Thermoset , Silicone , Silicone Rubber , Silicone, Molded, Glass Fiber Filled |
Manufacturer | Arlon |
Trade Name | Thermabond® |
Port | Ningbo port,China |
Trade Terms | FOB, CFR, CIF |
Payment Terms | L/C, T/T, Western Union |
Download PDF | Arlon Thermabond® 99A90X008 0.008" (0.203 mm) Uncured Silicone Rubber with PTFE Coated Fiberglass Carrier.pdf |
Price | EMAIL US sales@lookpolymers.com |
Physical Properties | Metric | English | Comments |
---|---|---|---|
Density | 1.85 g/cc | 0.0668 lb/in³ | Silicone Property; Arlon SQA-TMS-024 |
Thickness | 25.4 microns | 1.00 mil | Liner |
76.2 microns | 3.00 mil | Carrier | |
203 microns | 8.00 mil | Overall; Arlon SQA-TMS-003 |
Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Hardness, Shore A | 87 | 87 | Silicone Property; ASTM D2240 |
Tensile Strength | 2.52 MPa | 365 psi | Silicone Property; ASTM D412 |
Tensile Strength, Yield | 62.1 MPa @Strain <=1.00 % |
9000 psi @Strain <=1.00 % |
Silicone Property; Arlon SQA-TMS-008 |
Elongation at Break | 28 % | 28 % | Silicone Property; ASTM D412 |
Poissons Ratio | 0.50 | 0.50 | Approximately, Silicone Property |
Shear Modulus | 1.83 GPa @Strain <=100 % |
265 ksi @Strain <=100 % |
ASTM D1002 |
Shear Strength | 0.965 MPa | 140 psi | Lap Shear Strength; ASTM D1002 |
Thermal Properties | Metric | English | Comments |
---|---|---|---|
CTE, linear | 52.0 µm/m-°C @Temperature 20.0 - 160 °C |
28.9 µin/in-°F @Temperature 68.0 - 320 °F |
Silicone Property; ASTM E 831 |
Specific Heat Capacity | 0.850 J/g-°C @Temperature 100 °C |
0.203 BTU/lb-°F @Temperature 212 °F |
Silicone Property; ASTM E 1952 |
Thermal Conductivity | 3.00 W/m-K @Temperature 100 °C |
20.8 BTU-in/hr-ft²-°F @Temperature 212 °F |
Silicone Property; ASTM E 1530 |
3.40 W/m-K @Pressure 30.0 MPa, Temperature 50.0 °C |
23.6 BTU-in/hr-ft²-°F @Pressure 4350 psi, Temperature 122 °F |
Product Property; Arlon SQA-TMS-054 | |
Maximum Service Temperature, Air | 204.0 °C | 399.2 °F | |
Minimum Service Temperature, Air | -100 °C | -148 °F | |
Glass Transition Temp, Tg | -119 °C | -182 °F | Silicone Property; ASTM D3418 |
Electrical Properties | Metric | English | Comments |
---|---|---|---|
Dielectric Constant | 4.6 @Frequency 1.00e+6 Hz |
4.6 @Frequency 1.00e+6 Hz |
D<sub>k</sub>, Silicone Property; IPC TM 650-2.5.5.3 |
Dielectric Strength | 35.4 kV/mm | 900 kV/in | ASTM D149 |
Dissipation Factor | 0.0041 @Frequency 1.00e+6 Hz |
0.0041 @Frequency 1.00e+6 Hz |
D<sub>f</sub>, Silicone Property; IPC TM 650-2.5.5.3 |
Processing Properties | Metric | English | Comments |
---|---|---|---|
Cure Time | 15.0 min @Pressure 0.345 MPa, Temperature 121.0 °C |
0.250 hour @Pressure 50.0 psi, Temperature 249.8 °F |
Recommended Cure Cycle |
Shelf Life | 6.00 Month @Temperature 4.00 - 10.0 °C |
6.00 Month @Temperature 39.2 - 50.0 °F |
From date of manufacture |
Descriptive Properties | Value | Comments |
---|---|---|
Color | Gray | |
Plasticity | 7.1 mm | Arlon SQA-TMS-005 |
Total Product Weight (g/m2) | 376 | Arlon SQA-TMS-025 |