Arlon Thermabond® 48A51X015 0.015" (0.381 mm) Uncured Silicone Rubber with Fiberglass Substrate

Category	Polymer , Thermoset , Silicone , Silicone Rubber , Silicone, Molded, Glass Fiber Filled
Manufacturer	Arlon
Trade Name	Thermabond®
Port	Ningbo port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	Arlon Thermabond® 48A51X015 0.015" (0.381 mm) Uncured Silicone Rubber with Fiberglass Substrate.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

Description: Primerless Thermabond® Electrically insulating, thermally conductive, electronic adhesive. Bonds without primer.Design/Construction: Liner 1: Polyethylene Side 1: Uncured Silicone RubberSubstrate: Style 1080 FiberglassSide 2: Uncured Silicone RubberLiner 2: Polyethylene Product Use: Adhesive, thermally conductiveAppearance: High viscosity gum (pink) of fiberglass fabric with yellow release linersThis data represents typical values for the production material. The data should not be used to write, or in place of, material specifications.Information provided by Arlon, Silicone Technologies Division

Physical Properties	Metric	English	Comments
Density	2.80 g/cc	0.101 lb/in³	Silicone Property; Arlon SQA-TMS-024
Thickness	38.1 microns	1.50 mil	Liner 1
	38.1 microns	1.50 mil	Liner 2
	76.2 microns	3.00 mil	Substrate; Arlon SQA-TMS-003
	152 microns	6.00 mil	Side 1; Arlon SQA-TMS-003
	152 microns	6.00 mil	Side 2; Arlon SQA-TMS-003
	381 microns	15.0 mil	Overall; Arlon SQA-TMS-003

Mechanical Properties	Metric	English	Comments
Hardness, Shore A	77	77	Silicone Property; ASTM D2240
Tensile Strength	4.72 MPa	685 psi	Silicone Property; ASTM D412
Tensile Strength, Yield	24.5 MPa @Strain <=1.00 %	3550 psi @Strain <=1.00 %	Silicone Property; Arlon SQA-TMS-008
Elongation at Break	125 %	125 %	Silicone Property; ASTM D412
Poissons Ratio	0.50	0.50	Approximately, Silicone Property
Shear Modulus	0.000296 GPa @Strain <=25.0 %	0.0430 ksi @Strain <=25.0 %	ASTM D1002
Shear Strength	6.05 MPa	878 psi	Lap; ASTM 1002

Thermal Properties	Metric	English	Comments
CTE, linear	11.0 µm/m-°C @Temperature 20.0 - 160 °C	6.11 µin/in-°F @Temperature 68.0 - 320 °F	Silicone Property; ASTM E 831
Specific Heat Capacity	0.820 J/g-°C @Temperature 100 °C	0.196 BTU/lb-°F @Temperature 212 °F	Silicone Property; Arlon SQA-TMS-052
Thermal Conductivity	1.40 W/m-K @Temperature 100 °C	9.72 BTU-in/hr-ft²-°F @Temperature 212 °F	Silicone Property; ASTM E 1530
	1.50 W/m-K @Pressure 30.0 MPa, Temperature 50.0 °C	10.4 BTU-in/hr-ft²-°F @Pressure 4350 psi, Temperature 122 °F	Product Property; Arlon SQA-TMS-054
Maximum Service Temperature, Air	95.6 °C	204 °F
Minimum Service Temperature, Air	-73.3 °C	-100 °F
Glass Transition Temp, Tg	-118 °C	-180 °F
Flammability, UL94	V-0	V-0

Electrical Properties	Metric	English	Comments
Dielectric Constant	6.91 @Frequency 1.00e+6 Hz	6.91 @Frequency 1.00e+6 Hz	Silicon Property; IPC TM 650 - 2.5.5.3
Dielectric Strength	34.7 kV/mm	882 kV/in	ASTM D149
Dissipation Factor	0.0044 @Frequency 1.00e+6 Hz	0.0044 @Frequency 1.00e+6 Hz	Silicon Property; IPC TM 650 - 2.5.5.3

Processing Properties	Metric	English	Comments
Cure Time	15.0 min @Temperature 121 °C	0.250 hour @Temperature 250 °F	Recommended Cure Cycle
Shelf Life	6.00 Month @Temperature 4.00 - 10.0 °C	6.00 Month @Temperature 39.2 - 50.0 °F	From date of manufacture

Descriptive Properties	Value	Comments
Color	Gray
Plasticity	2.3 mm	Arlon-SQA-TMS-005
Total Product Weight (g/m2)	550	Arlon SQA-TMS-025