Arlon R37806X030 Silicone Rubber/Fiberglass
| Category | Polymer , Thermoset , Rubber or Thermoset Elastomer (TSE) , Silicone , Silicone Rubber , Silicone, Molded, Glass Fiber Filled |
| Manufacturer | Arlon |
| Trade Name | |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Arlon R37806X030 Silicone Rubber/Fiberglass.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Interleave: 3 mil PE; Side 2: uncured silicone rubber; Substrate: 162 fiberglass; Side 1: cured silicone rubber
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 2.80 g/cc | 2.80 g/cc | silicone property; Arlon SQA-TMS-024 |
| Thickness | 76.2 microns | 3.00 mil | side 1; Arlon SQA-TMS-003 |
| 229 microns | 9.00 mil | side 2; Arlon SQA-TMS-003 | |
| 457 microns | 18.0 mil | substrate; Arlon SQA-TMS-003 | |
| 762 microns | 30.0 mil | overall; Arlon SQA-TMS-003 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Shore A | 77 | 77 | silicone property; ASTM D2240 |
| Tensile Strength, Ultimate | 4.72 MPa | 685 psi | silicone property; ASTM D412 |
| Elongation at Break | 125 % | 125 % | silicone property; ASTM D412 |
| Modulus of Elasticity | 0.0245 GPa | 3.55 ksi | Arlon SQA-TMS-008 |
| Poissons Ratio | 0.50 | 0.50 | |
| Adhesive Bond Strength | 0.0241 MPa | 3.50 psi | Arlon SQA-TMS-011 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 111 µm/m-°C @Temperature 20.0 °C |
61.7 µin/in-°F @Temperature 68.0 °F |
silicone property; ASTM E 831 |
| Specific Heat Capacity | 0.820 J/g-°C @Temperature 100 °C |
0.196 BTU/lb-°F @Temperature 212 °F |
silicone property; Arlon SQA-TMS-052 |
| Thermal Conductivity | 1.40 W/m-K | 9.72 BTU-in/hr-ft²-°F | silicone property; ASTM E1530 |
| 1.54 W/m-K @Temperature 100 °C |
10.7 BTU-in/hr-ft²-°F @Temperature 212 °F |
overall; Arlon SQA-TMS-054 | |
| Maximum Service Temperature, Air | 200 °C | 392 °F | |
| Minimum Service Temperature, Air | -100 °C | -148 °F | |
| Glass Transition Temp, Tg | -118 °C | -180 °F | silicone property; ASTM D3418 |
| Flammability, UL94 | V-0 | V-0 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Dielectric Constant | 6.91 @Frequency 1.00e+6 Hz |
6.91 @Frequency 1.00e+6 Hz |
silicone property; IPC TM 650-2.5.5.3 |
| Dielectric Strength | 17.7 kV/mm | 450 kV/in | ASTM D149 |
| Dissipation Factor | 0.0044 @Frequency 1.00e+6 Hz |
0.0044 @Frequency 1.00e+6 Hz |
silicone property; IPC TM 650-2.5.5.3 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Cure Time | 15.0 min @Temperature 121 °C |
0.250 hour @Temperature 250 °F |
|
| 120 min @Temperature 200 °C |
2.00 hour @Temperature 392 °F |
||
| Shelf Life | 6.00 Month @Temperature 7.22 °C |
6.00 Month @Temperature 45.0 °F |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Color | Gray | |
| Plasticity (mm) Arlon SQA-TMS-005 | silicone property |
Users viewing this material also viewed the following:
- Ineos ABS NOVODUR® P2L-AT ABS, Injection Grade (discontinued **)
- DuPont Elvax® 3174 Ethylene-Vinyl Acetate Copolymer Resin for Coextrusion, Cast Film (discontinued **)
- Honeywell ACLAR® 11A (2.00 mil) CTFE Homopolymer, Barrier Film (discontinued **)
- LG Chemical SEETEC M1500 Polypropylene Impact Copolymer
- SolVin 250SB Polyvinyl Chloride General Purpose - Rigid
- Unipetrol Middle Oil Hydrogenate
- 3M Cushion-Mount™ E1040 Plus Plate Mounting Tapes with Easy Mount Adhesive and High Plateside Adhesion
- Solvay Specialty Polymers Hylar® 5000 Polyvinylidene Fluoride (PVDF) (Unverified Data**)
- ExxonMobil Mobil Delvac 10W-30 Synthetic Transmission Fluid Arctic
Copyright © lookpolymers.com All Rights Reserved