Arkema Group Rilsan® BESN P40 W5 TL Nylon 11, Flexible Tubing Grade (Conditioned)

Category	Polymer , Thermoplastic , Nylon , Nylon 11 , Nylon 11, Flexible Tubing Grade
Manufacturer	Arkema
Trade Name
Port	Ningbo port,China
Trade Terms	EXW, FOB, CFR, CIF
Payment Terms	L/C, T/T, PayPal
Download PDF	Arkema Group Rilsan® BESN P40 W5 TL Nylon 11, Flexible Tubing Grade (Conditioned).pdf
Price	EMAIL US sales@lookpolymers.com

Material Notes:

Designation ISO 1874-PA11-P,EFHL,22-003Flexible grade for tubes extrusion. Available color: milky white. Light and heat stabilized. Flame retardant agent.Fire-resistant. Flexibility. High impact strength. Very good chemical resistance. Ability to be processed at high speed.Example applications: Flexible tubes for automotive.ISO data provided by the manufacturer, Arkema.

Physical Properties	Metric	English	Comments
Density	1.08 g/cc	0.0390 lb/in³
Melt Flow	7.9 g/10 min <br>@Load 2.16 kg,<br> Temperature 235 °C	7.9 g/10 min <br>@Load 4.76 lb,<br> Temperature 455 °F

Mechanical Properties	Metric	English	Comments
Tensile Strength, Yield	27.0 MPa	3920 psi	50 mm/min
Elongation at Break	>= 50 %	>= 50 %	Nominal Strain; 50 mm/min
Elongation at Yield	35 %	35 %	50 mm/min
Tensile Modulus	0.580 GPa	84.1 ksi	1 mm/min
Charpy Impact Unnotched	NB	NB
	NB	NB	Low Temp
Charpy Impact, Notched	NB	NB
	0.420 J/cm² <br>@Temperature -30.0 °C	2.00 ft-lb/in² <br>@Temperature -22.0 °F

Thermal Properties	Metric	English	Comments
CTE, linear, Parallel to Flow	110 µm/m-°C <br>@Temperature 20.0 °C	61.1 µin/in-°F <br>@Temperature 68.0 °F
Melting Point	178 °C	352 °F	(Dry)
Deflection Temperature at 0.46 MPa (66 psi)	147 °C	297 °F
Deflection Temperature at 1.8 MPa (264 psi)	55.0 °C	131 °F
Vicat Softening Point	136 °C	277 °F	50°C/hr; 50N
Flammability, UL94	V-2 <br>@Thickness 1.60 mm	V-2 <br>@Thickness 0.0630 in
	V-2 <br>@Thickness 3.20 mm	V-2 <br>@Thickness 0.126 in
Oxygen Index	27 %	27 %

Electrical Properties	Metric	English	Comments
Dielectric Strength	18.0 kV/mm	457 kV/in
Comparative Tracking Index	600 V	600 V

Users viewing this material also viewed the following: