- Diallyl Phthalate (DAP) Molding Compound, Short Glass Fiber Filled
- Sumitomo Bakelite North America RX® 1-520/RX® 1310 Short-Glass Reinforced Diallyl Phthalate
Sumitomo Bakelite North America RX® 1-520/RX® 1310 Short-Glass Reinforced Diallyl Phthalate
| Category | Polymer , Thermoset , Diallyl Phthalate (DAP) , Diallyl Phthalate (DAP) Molding Compound, Short Glass Fiber Filled , Filled/Reinforced Thermoset |
| Manufacturer | Sumitomo Bakelite North America |
| Trade Name | |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Sumitomo Bakelite North America RX® 1-520/RX® 1310 Short-Glass Reinforced Diallyl Phthalate.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Short glass fiber reinforced, non-flame retardant, diallyl ortho-phthalate molding compound which meets the requirements of ASTM D5948 Type SDG.Information provided by Vyncolit, a Sumitomo Bak Group
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Bulk Density | 0.750 g/cc | 0.0271 lb/in³ | Powder Density; ASTM D1895 |
| Density | 1.83 g/cc | 0.0661 lb/in³ | Relative Density; ASTM D792 |
| Linear Mold Shrinkage | 0.0010 - 0.0030 cm/cm | 0.0010 - 0.0030 in/in | Compression Molding; ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 76.0 MPa | 11000 psi | ASTM D638 |
| Flexural Strength | 124 MPa | 18000 psi | At Rupture; ASTM D790 |
| Flexural Modulus | 12.4 GPa | 1800 ksi | ASTM D790 |
| Compressive Strength | 150 MPa | 21800 psi | ASTM D695 |
| Izod Impact, Notched | 0.370 J/cm | 0.693 ft-lb/in | ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 21.0 µm/m-°C @Temperature 20.0 °C |
11.7 µin/in-°F @Temperature 68.0 °F |
ASTM E-831 |
| Thermal Conductivity | 0.280 W/m-K | 1.94 BTU-in/hr-ft²-°F | ASTM C-518 |
| Maximum Service Temperature, Air | 130 °C | 266 °F | UL 746B |
| Deflection Temperature at 1.8 MPa (264 psi) | 205 °C | 401 °F | As molded; ASTM D648 |
| Oxygen Index | 26 % | 26 % | ASTM D2863 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Dielectric Constant | 3.5 @Frequency 1e+6 Hz |
3.5 @Frequency 1e+6 Hz |
Wet; ASTM D150 |
| 4.0 @Frequency 1000 Hz |
4.0 @Frequency 1000 Hz |
wet; ASTM D150 | |
| Dielectric Strength | 12.2 kV/mm | 310 kV/in | 60Hz, Step-by-Step, wet; ASTM D149 |
| Dissipation Factor | 0.0090 @Frequency 1000 Hz |
0.0090 @Frequency 1000 Hz |
wet; ASTM D150 |
| 0.016 @Frequency 1e+6 Hz |
0.016 @Frequency 1e+6 Hz |
wet; ASTM D150 | |
| Arc Resistance | 130 sec | 130 sec | ASTM D495 |
| Comparative Tracking Index | >= 600 V | >= 600 V | IEC 112 |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Color | Black, Brown, Green | |
| Form | Granular | |
| Main Filler | Glass Fiber | |
| Molding Method | Compression, transfer, injection |
Users viewing this material also viewed the following:
- Nye Lubricants 500S (RT) Synthetic Oil
- SABIC Innovative Plastics GELOY XP7560 ASA (Europe-Africa-Middle East)
- Karina 850-10/99-Y-ERYB White PVC Compound
- Schott N-SF2 Glass
- Solvay Chemicals NOCOLOK® Flux Drystatic Potassium Fluoroaluminate
- SABIC Innovative Plastics LNP Thermocomp M10009A PP (Europe-Africa-Middle East)
- Westlake Epolene® N-14P Nonemulsifiable - Low Molecular Weight Polyethylene Polymer
- Beijing Evergrow Resources ASHRAE HEPA-W29 Glass Fiber Paper
- Bulk Molding Compounds BMC 620 Mineral Filled, Glass Fiber Reinforced Polyester Compound
Copyright © lookpolymers.com All Rights Reserved