Arkema Group Rilsan® BECN W3 TL Nylon 11, Sheathing Grade (Conditioned)

Category	Polymer , Thermoplastic , Nylon , Nylon 11 , Nylon 11, Cable Sheathing Grade
Manufacturer	Arkema
Trade Name
Port	Shanghai port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	Arkema Group Rilsan® BECN W3 TL Nylon 11, Sheathing Grade (Conditioned).pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

Designation ISO 1874-PA11,KFHL,12-010Rigid grade for sheathing wires and cables. Available color: natural. Light and heat stabilized. Flame retardant agent.Fire-resistant. High abrasion resistance. Well adapted melt viscosity. Ability to be processed in thin wall thickness. Easy to color.Example applications: Coating of electrical and telephone cable.ISO data provided by the manufacturer, Arkema.

Physical Properties	Metric	English	Comments
Density	1.11 g/cc	0.0401 lb/in³
Melt Flow	27.5 g/10 min @Load 2.16 kg, Temperature 235 °C	27.5 g/10 min @Load 4.76 lb, Temperature 455 °F

Mechanical Properties	Metric	English	Comments
Tensile Strength, Yield	43.0 MPa	6240 psi	50 mm/min
Elongation at Break	>= 50 %	>= 50 %	Nominal Strain; 50 mm/min
Elongation at Yield	6.0 %	6.0 %	50 mm/min
Tensile Modulus	1.86 GPa	270 ksi	1 mm/min

Thermal Properties	Metric	English	Comments
CTE, linear, Parallel to Flow	100 µm/m-°C @Temperature 20.0 °C	55.6 µin/in-°F @Temperature 68.0 °F
Melting Point	183 °C	361 °F	(Dry)
Deflection Temperature at 0.46 MPa (66 psi)	156 °C	313 °F
Deflection Temperature at 1.8 MPa (264 psi)	52.0 °C	126 °F
Vicat Softening Point	165 °C	329 °F	50°C/hr; 50N
Flammability, UL94	V-2 @Thickness 1.60 mm	V-2 @Thickness 0.0630 in
	V-2 @Thickness 3.20 mm	V-2 @Thickness 0.126 in
Oxygen Index	30 %	30 %

Electrical Properties	Metric	English
Electrical Resistivity	1.00e+14 ohm-cm	1.00e+14 ohm-cm
Surface Resistance	1.00e+14 ohm	1.00e+14 ohm
Dielectric Strength	20.0 kV/mm	508 kV/in
Comparative Tracking Index	600 V	600 V