Category | Polymer , Thermoset , Fluoropolymer, TS , Rubber or Thermoset Elastomer (TSE) |
Manufacturer | 3M Dyneon™ |
Trade Name | |
Port | Shanghai port,China |
Trade Terms | FOB, CFR, CIF |
Payment Terms | L/C, T/T, Western Union |
Download PDF | 3M Dyneon™ FC 2211 Fluoroelastomer.pdf ![]() |
Price | EMAIL US sales@lookpolymers.com |
Physical Properties | Metric | English | Comments |
---|---|---|---|
Specific Gravity | 1.80 g/cc | 1.80 g/cc | |
Mooney Viscosity | 20 @Temperature 121 °C |
20 @Temperature 250 °F |
ML1+10 |
Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Hardness, Shore A | 75 | 75 | Press Cure 7 minutes @ 177°C, Post Cure 24 hours @ 260°C; ASTM D2240 |
Tensile Strength at Break | 12.9 MPa | 1870 psi | Press Cure 7 minutes @ 177°C, Post Cure 24 hours @ 260°C |
Elongation at Break | 180 % | 180 % | Press Cure 7 minutes @ 177°C, Post Cure 24 hours @ 260°C |
100% Modulus | 0.00414 GPa | 0.600 ksi | Press Cure 7 minutes @ 177°C, Post Cure 24 hours @ 260°C |
Compression Set | 17 % | 17 % | Aged 70 hours @ 200°C, -214 O-rings; ASTM D395 Method B |
Thermal Properties | Metric | English | Comments |
---|---|---|---|
Transformation Temperature | -18.0 °C | -0.400 °F | TR10; ASTM D1329 |
Component Elements Properties | Metric | English | Comments |
---|---|---|---|
Fluorine, F | 65.9 % | 65.9 % |
Descriptive Properties | Value | Comments |
---|---|---|
Color | Translucent to Off-White | |
MH, Maximum Torque, inch-lb @ 177°C | 14 inch-lb | 100 cpm, 0.5° Arc, 6 Minutes @ 177°C |
ML, Minimum Torque | 0.3 inch-lb | 100 cpm, 0.5° Arc, 6 Minutes @ 177°C |
Solubility | Ketones and Esters | |
t`50, Time to 50% cure | 2.5 minutes | 100 cpm, 0.5° Arc, 6 Minutes @ 177°C |
t`90 - Time to 90% cure @ 177°C - minutes | 3.8 minutes | 100 cpm, 0.5° Arc, 6 Minutes @ 177°C |
ts2 - Time to 2 in-lb rise from min @ 177°C - min | 2.2 minutes | 100 cpm, 0.5° Arc, 6 Minutes @ 177°C |