- Arkema Group Rilsan® AUM 30 T6LD Nylon 12, 30% Glass Bead Filled (Dry)
Arkema Group Rilsan® AUM 30 T6LD Nylon 12, 30% Glass Bead Filled (Dry)
| Category | Polymer , Thermoplastic , Nylon , Nylon 12 , Nylon 12, Glass Bead Filled |
| Manufacturer | Arkema |
| Trade Name | |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Arkema Group Rilsan® AUM 30 T6LD Nylon 12, 30% Glass Bead Filled (Dry).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Designation ISO 1874-PA12,MHLR,16-020,GB30Rigid grad with glass beads filler (30%) for injection molding. Available colors: black and natural. Light and heat stabilized. Mold-release agent.Reinforced isotropic performances. High compressive strength. Very low shrinkage: include 0,5% on average for the design of the mold. High dimensional stability (low moisture absorption). Low coefficient of linear expansion.Example applications: Mechanical parts with dimensional precision.ISO data provided by the manufacturer, Arkema.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.22 g/cc | 0.0441 lb/in³ | |
| Water Absorption | 1.2 % | 1.2 % | |
| Melt Flow | 70.8 g/10 min @Load 2.16 kg, Temperature 235 °C |
70.8 g/10 min @Load 4.76 lb, Temperature 455 °F |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 42.0 MPa | 6090 psi | 50 mm/min |
| Elongation at Break | 24 % | 24 % | Nominal Strain; 50 mm/min |
| Elongation at Yield | 5.0 % | 5.0 % | 50 mm/min |
| Tensile Modulus | 2.04 GPa | 296 ksi | 1 mm/min |
| Charpy Impact Unnotched | 3.80 J/cm² | 18.1 ft-lb/in² | |
| 4.45 J/cm² @Temperature -30.0 °C |
21.2 ft-lb/in² @Temperature -22.0 °F |
||
| Charpy Impact, Notched | 0.500 J/cm² | 2.38 ft-lb/in² | |
| 0.460 J/cm² @Temperature -30.0 °C |
2.19 ft-lb/in² @Temperature -22.0 °F |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Melting Point | 174 °C | 345 °F | 10°C/min |
| Flammability, UL94 | HB @Thickness 1.60 mm |
HB @Thickness 0.0630 in |
|
| HB @Thickness 3.10 mm |
HB @Thickness 0.122 in |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Dissipation Factor | 0.00029 @Frequency 1e+6 Hz |
0.00029 @Frequency 1e+6 Hz |
|
| 0.00045 @Frequency 100 Hz |
0.00045 @Frequency 100 Hz |
Users viewing this material also viewed the following:
- Plastcom SLOVALEN PC 59 GF 13 Compounded Polypropylene Homopolymer, 13% Chemically Coupled Glass Fiber
- Radici Heraflex® E 3918 TPC-ET Thermoplastic Elastomer
- Lucas-Milhaupt Clean & Bright 6 Tin/ Silver Solder
- Styrolution Absolac® 30GF15 ABS, 15% Glass Filled
- A. Schulman POLYBATCH™ 60186U Almond Concentrate Based in LLDPE
- TSE Industries Millathane® CM Millable Polyether Urethane Rubber with Plastolein 9057 Plasticizer
- Total PPH 3825 Polypropylene, Injection Molding Grade
- Cytec Conathane® CC-1155-35 (Conap) Polyurethane Two-component Dielectric Conformal Coating
- ExxonMobil Label-Lyte™ 50LGT702 OPP Film
Copyright © lookpolymers.com All Rights Reserved