SABIC Innovative Plastics LNP THERMOCOMP UF0069S PPA
| Category | Polymer , Thermoplastic , Polyphthalamide (PPA) |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | LNP THERMOCOMP |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics LNP THERMOCOMP UF0069S PPA.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
LNP THERMOCOMP* UF0069S is a compound based on Polyphthalamide resin containing 30% Glass Fiber. Added features of this material include: Flame Retardant, Heat Stabilized.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.65 g/cc | 0.0596 lb/in³ | ISO 1183 |
| 1.655 g/cc | 0.05979 lb/in³ | ASTM D792 | |
| Moisture Absorption | 0.240 % | 0.240 % | 50% RH, 24 hrs; ASTM D570 |
| 0.260 % | 0.260 % | 23°C / 50% RH; ISO 62 | |
| Linear Mold Shrinkage, Flow | 0.0020 cm/cm @Time 86400 sec |
0.0020 in/in @Time 24.0 hour |
ASTM D955 |
| 0.0022 cm/cm @Time 86400 sec |
0.0022 in/in @Time 24.0 hour |
ISO 294 | |
| Linear Mold Shrinkage, Transverse | 0.0059 cm/cm @Time 86400 sec |
0.0059 in/in @Time 24.0 hour |
ISO 294 |
| 0.0060 cm/cm @Time 86400 sec |
0.0060 in/in @Time 24.0 hour |
ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 166 MPa | 24100 psi | ISO 527 |
| 181 MPa | 26300 psi | ASTM D638 | |
| Elongation at Break | 1.7 % | 1.7 % | ISO 527 |
| 1.9 % | 1.9 % | ASTM D638 | |
| Tensile Modulus | 12.07 GPa | 1751 ksi | 1 mm/min; ISO 527 |
| 13.78 GPa | 1999 ksi | 50 mm/min; ASTM D638 | |
| Flexural Strength | 258 MPa | 37400 psi | ASTM D790 |
| 264 MPa | 38300 psi | ISO 178 | |
| Flexural Modulus | 12.06 GPa | 1749 ksi | ASTM D790 |
| 12.32 GPa | 1787 ksi | ISO 178 | |
| Izod Impact, Notched | 0.900 J/cm | 1.69 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | 5.50 J/cm | 10.3 ft-lb/in | ASTM D4812 |
| Izod Impact, Notched (ISO) | 9.00 kJ/m² | 4.28 ft-lb/in² | 80*10*4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 44.0 kJ/m² | 20.9 ft-lb/in² | 80*10*4; ISO 180/1U |
| Dart Drop, Total Energy | 2.00 J | 1.48 ft-lb | Instrumented Impact Energy @ peak; ASTM D3763 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Flammability, UL94 | V-0 @Thickness 1.50 mm |
V-0 @Thickness 0.0591 in |
UL 94 |
| 5VA @Thickness 1.50 mm |
5VA @Thickness 0.0591 in |
UL 94 |
Users viewing this material also viewed the following:
- Nilit FRIANYL B63 KF30 Nylon 6 for injection molding, 30% short glass fiber reinforced
- PolyOne Geon™ Vinyl Flexible XV3887 Polyvinyl Chloride, Flexible (PVC, Flexible)
- Entec Hypel® PELLD20/.925 LLDPE (discontinued **)
- Flint Hills P6G2Z-090 Impact Copolymer Polypropylene
- LATI Latene® 11 MDT05-01 PP Homopolymer
- Sylvin Technologies 8999-80 Natural PVC Extrusion Compound
- Chase Plastics CP Pryme® NN113GL (COND, 50% RH) Nylon 66, 13% Glass Fiber Reinforced, Internally Lubricated
- Toyobo Zylon® HM Poly(p-phenylene-2,6-benzobisoxazole) Fiber
- California Fine Wire Nickel Alloy 30 Copper Nickel Resistance Wire
- ArcelorMittal FB 450 Hot rolled ferrite-bainite steel
Copyright © lookpolymers.com All Rights Reserved