Arkema Group Rilsan® AESN P40 TL Nylon 12, Flexible Tubing Grade (Conditioned)
| Category | Polymer , Thermoplastic , Nylon , Nylon 12 , Nylon 12, Extrusion/Tubing Grade |
| Manufacturer | Arkema |
| Trade Name | |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Arkema Group Rilsan® AESN P40 TL Nylon 12, Flexible Tubing Grade (Conditioned).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Designation ISO 1874-PA12-P,EHL,22-004Flexible grade for tubes extrusion. Available colors: black and natural. Light and heat stabilized.High impact strength. High burst pressure. Very good chemical resistance. Easy to be processed.Example applications: Pneumatic control tubes, Fuel line.ISO data provided by the manufacturer, Arkema.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.04 g/cc | 0.0376 lb/in³ | |
| Melt Flow | 5.6 g/10 min @Load 2.16 kg, Temperature 235 °C |
5.6 g/10 min @Load 4.76 lb, Temperature 455 °F |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 24.0 MPa | 3480 psi | 50 mm/min |
| Elongation at Break | >= 50 % | >= 50 % | Nominal Strain; 50 mm/min |
| Elongation at Yield | 25 % | 25 % | 50 mm/min |
| Tensile Modulus | 0.415 GPa | 60.2 ksi | 1 mm/min |
| Charpy Impact Unnotched | NB | NB | |
| NB | NB | Low Temp | |
| Charpy Impact, Notched | NB | NB | |
| 0.390 J/cm² @Temperature -30.0 °C |
1.86 ft-lb/in² @Temperature -22.0 °F |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 140 µm/m-°C @Temperature 20.0 °C |
77.8 µin/in-°F @Temperature 68.0 °F |
|
| Melting Point | 168 °C | 334 °F | (Dry) |
| Deflection Temperature at 0.46 MPa (66 psi) | 125 °C | 257 °F | |
| Deflection Temperature at 1.8 MPa (264 psi) | 46.0 °C | 115 °F | |
| Vicat Softening Point | 130 °C | 266 °F | 50°C/hr; 50N |
| Flammability, UL94 | HB @Thickness 1.60 mm |
HB @Thickness 0.0630 in |
|
| HB @Thickness 3.20 mm |
HB @Thickness 0.126 in |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Electrical Resistivity | 1.00e+11 ohm-cm | 1.00e+11 ohm-cm | |
| Surface Resistance | 5.00e+11 ohm | 5.00e+11 ohm | |
| Dielectric Strength | 24.0 kV/mm | 610 kV/in | |
| Comparative Tracking Index | 600 V | 600 V |
Users viewing this material also viewed the following:
- Overview of materials for Polystyrene, Glass Filled
- Mitsubishi Xantar® G4F 22 R Polycarbonate-20% Glass Reinforced
- Karina 34/151-IE MBU Lilac Color Concentrate
- Karina 67/200-D-IS-SD Clear PVC Compound
- Techmer ES HiFill® ABS GB15 15% Glass Bead Filler
- SABIC Innovative Plastics LNP THERMOCOMP Noryl_FM4025 PPE+PS
- ExxonMobil ESCOREZ™ 5415 Petroleum Hydrocarbon Resin
- Cheng Yu Plastic FR200GV30 Flame Retardant Nylon 66, 30% Glass Fiber
- Momentive Performance Materials PolarTherm® PT180 Boron Nitride (BN) Powder
- DuPont Performance Polymers Zytel® HTN 52G35HSL BK083 Polyphthalamide (PPA) (Unverified Data**)
Copyright © lookpolymers.com All Rights Reserved