Arkema Group Orgalloy® LE 60SF Flexible Nylon Alloy (Conditioned)

Category	Polymer , Thermoplastic , Nylon , Nylon, Flexible Alloy
Manufacturer	Arkema
Trade Name	Orgalloy®
Port	Ningbo port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	Arkema Group Orgalloy® LE 60SF Flexible Nylon Alloy (Conditioned).pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

LE series, flexible polyamide alloys: processability on PE screw, low moisture absorption, chemical resistance (no known solvents).lower in viscosity than LE 6000, adapted to Suited to the cast film extrusion. Injection molding is also possibleISO data provided by the manufacturer, Arkema.

Physical Properties	Metric	English	Comments
Density	1.04 g/cc	0.0376 lb/in³
Water Absorption	5.5 %	5.5 %
Moisture Absorption at Equilibrium	1.8 %	1.8 %	Humidity Absorption
Melt Flow	6.0 g/10 min @Load 2.16 kg, Temperature 235 °C	6.0 g/10 min @Load 4.76 lb, Temperature 455 °F

Mechanical Properties	Metric	English	Comments
Tensile Strength, Yield	36.0 MPa	5220 psi	50 mm/min
Elongation at Break	>= 50 %	>= 50 %	Nominal Strain; 50 mm/min
Elongation at Yield	4.0 %	4.0 %	50 mm/min
Tensile Modulus	1.35 GPa	196 ksi	1 mm/min
Tensile Creep Modulus, 1 hour	1150 MPa	167000 psi
Tensile Creep Modulus, 1000 hours	550 MPa	79800 psi

Thermal Properties	Metric	English	Comments
Melting Point	220 °C	428 °F	10°C/min
Vicat Softening Point	99.0 °C	210 °F	50°C/hr; 50N
Flammability, UL94	HB @Thickness 1.60 mm	HB @Thickness 0.0630 in
	HB @Thickness 3.20 mm	HB @Thickness 0.126 in

Electrical Properties	Metric	English	Comments
Comparative Tracking Index	600 V	600 V