Aremco HiE-Coat™ 840-CM High Emissivity Coating, Inorganic-Ceramic Filled
| Category | Ceramic , Other Engineering Material , Ceramic/Metallic Coating |
| Manufacturer | Aremco |
| Trade Name | HiE-Coat™ |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Aremco HiE-Coat™ 840-CM High Emissivity Coating, Inorganic-Ceramic Filled.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Ceramic-based, black-pigmented coating for dense refractories to 2500°F (1371°C) and stainless steel to 900°F (482°C)
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | >= 1.54 g/cc | >= 0.0556 lb/in³ | |
| Solids Content | 19.9 % | 19.9 % | by volume |
| 48.0 % | 48.0 % | by weight | |
| Volatile Organic Compounds (VOC) Content | 0.000 g/l | 0.000 g/l | |
| Viscosity | 600 - 800 cP | 600 - 800 cP | |
| Thickness | 25.4 microns | 1.00 mil | recommended dry film thickness |
| 128 microns | 5.03 mil | estimated wet film thickness | |
| Storage Temperature | 55.0 - 85.0 °C | 131 - 185 °F |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Maximum Service Temperature, Air | 482 °C | 900 °F | Stainless |
| 1370 °C | 2500 °F | Ceramics |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Processing Temperature | 50.0 - 90.0 °C | 122 - 194 °F | Application Temp |
| Cure Time | 30.0 min @Temperature 93.3 °C |
0.500 hour @Temperature 200 °F |
Step 1, preceeded by 1 hour air set |
| 60.0 min @Temperature 260 °C |
1.00 hour @Temperature 500 °F |
Step 2 | |
| Shelf Life | 6.00 Month @Temperature 12.8 - 29.4 °C |
6.00 Month @Temperature 55.0 - 85.0 °F |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Color | Jet Black | |
| Dry Film Coverage ft2/gal | 319 | at 1 mil |
| Thinner | 840CM-T |
Users viewing this material also viewed the following:
- Pacific Sintered Materials FX-226-T Infiltrated Iron Powdered Metal
- LATI Latamid 6 S/30 PA 6, 30% Glass Bead Reinforced
- A. Schulman POLYFORT™ PP 3045
- A. Schulman POLYFLAM™ RPP 1133 Flame Retardant, Copolymer Polypropylene
- A. Schulman PP 3449-01 Polypropylene Copolymer Polypropylene
- DuPont™ Surlyn® 8320 Ionomer Resin, Sodium
- Akzo Nobel Trigonox® HM Peroxide Cure Agent
- 3M XP2112 Hi-Performance Adhesive Transfer Tape
Copyright © lookpolymers.com All Rights Reserved