- HOME
- POLYMER SEARCH
- Thermoset
- Epoxy
- Aremco Aremco-Bond™ 2220 High Performance Epoxide
Aremco Aremco-Bond™ 2220 High Performance Epoxide
| Category | Polymer , Adhesive , Thermoset , Epoxy |
| Manufacturer | Aremco |
| Trade Name | Aremco-Bond™ |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Aremco Aremco-Bond™ 2220 High Performance Epoxide.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Ceramic-Filled, High Chemical Resistance, Machinable. For Repairing Deeply-Corroded Parts.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.70 g/cc | 1.70 g/cc |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Shore D | 88 | 88 | |
| Flexural Strength | 110 MPa | 16000 psi | ASTM D790 |
| Shear Strength | 18.6 MPa | 2700 psi | ASTM D1002-94 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 32.4 µm/m-°C @Temperature 20.0 °C |
18.0 µin/in-°F @Temperature 68.0 °F |
|
| Maximum Service Temperature, Air | 204 °C | 400 °F | |
| Minimum Service Temperature, Air | -55.0 °C | -67.0 °F | |
| Shrinkage | 0.30 % | 0.30 % | Cure Shrinkage |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 2.00e+15 ohm-cm | 2.00e+15 ohm-cm | |
| Dielectric Constant | 6.8 @Frequency 1000 Hz |
6.8 @Frequency 1000 Hz |
|
| Dielectric Strength | 18.9 kV/mm | 480 kV/in | |
| Dissipation Factor | 0.010 | 0.010 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Cure Time | 120 min @Temperature 93.3 °C |
2.00 hour @Temperature 200 °F |
Alternate Cure |
| 720 - 1440 min @Temperature 23.0 °C |
12.0 - 24.0 hour @Temperature 73.4 °F |
Recommended Cure | |
| Pot Life | 60.0 min @Temperature 25.0 °C |
60.0 min @Temperature 77.0 °F |
100 gm mass |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Chemical Resistance | Very Good | |
| Color | Black | |
| Mix Ratio By Weight | 100:28 | resin:hardener |
| Viscosity | Paste |
Users viewing this material also viewed the following:
- Plastcom SLOVALEN PC 51 GF 10 PP, 10% glass fibre
- Solvay Specialty Polymers Amodel® A-1230 L Polyphthalamide (PPA) (discontinued **)
- Nilit FRIANYL A63 HH-SG-GV 2020 Nylon 6.6 for injection molding, 20% mineral filled, 20% glass fiber reinforced
- Lanxess Pocan® B 3215 901510 PBT, 10% Glass Fiber
- Colorite Polymers 2007NAT Rigid PVC
- Arlon 56581R025 0.025" (0.635 mm) Uncured Silicone Rubber with Fiberglass Substrate
- BCC Products BC 100 Thick Cyanoacrylate Adhesive
- DSM Akulon® K-FHGM24 (Dry) 30% Glass/Mineral Reinforced, Nylon 6 (North America) (discontinued **)
- Chase Plastics CP Pryme® PPC100-8M Polypropylene Copolymer
Copyright © lookpolymers.com All Rights Reserved