SABIC Innovative Plastics LNP LUBRICOMP OX90351 PPS
| Category | Polymer , Thermoplastic , Polyphenylene Sulfide (PPS) |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | LNP LUBRICOMP |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics LNP LUBRICOMP OX90351 PPS.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
LNP LUBRICOMP* OX90351 is a compound based on Polyphenylene Sulfide resin containing Proprietary Filler(s). Added feature of this material is: Wear Resistant.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.67 g/cc | 0.0603 lb/in³ | ASTM D792 |
| 1.67 g/cc | 0.0603 lb/in³ | ISO 1183 | |
| Moisture Absorption | 0.0100 % | 0.0100 % | 50% RH, 24 hrs; ASTM D570 |
| 0.530 % | 0.530 % | 23°C / 50% RH; ISO 62 | |
| Linear Mold Shrinkage, Flow | 0.0020 cm/cm @Time 86400 sec |
0.0020 in/in @Time 24.0 hour |
ASTM D955 |
| 0.0022 cm/cm @Time 86400 sec |
0.0022 in/in @Time 24.0 hour |
ISO 294 | |
| Linear Mold Shrinkage, Transverse | 0.0060 cm/cm @Time 86400 sec |
0.0060 in/in @Time 24.0 hour |
ASTM D955 |
| 0.0060 cm/cm @Time 86400 sec |
0.0060 in/in @Time 24.0 hour |
ISO 294 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 96.0 MPa | 13900 psi | ISO 527 |
| 100 MPa | 14500 psi | ASTM D638 | |
| Elongation at Break | 1.5 % | 1.5 % | ASTM D638 |
| 1.5 % | 1.5 % | ISO 527 | |
| Tensile Modulus | 9.71 GPa | 1410 ksi | 1 mm/min; ISO 527 |
| 10.27 GPa | 1490 ksi | 50 mm/min; ASTM D638 | |
| Flexural Strength | 152 MPa | 22000 psi | ASTM D790 |
| 154 MPa | 22300 psi | ISO 178 | |
| Flexural Modulus | 9.17 GPa | 1330 ksi | ASTM D790 |
| 9.38 GPa | 1360 ksi | ISO 178 | |
| Izod Impact, Notched | 0.530 J/cm | 0.993 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | 3.84 J/cm | 7.19 ft-lb/in | ASTM D4812 |
| Izod Impact, Notched (ISO) | 6.00 kJ/m² | 2.86 ft-lb/in² | 80*10*4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 20.0 kJ/m² | 9.52 ft-lb/in² | 80*10*4; ISO 180/1U |
| Dart Drop, Total Energy | 2.00 J | 1.48 ft-lb | Instrumented Impact Energy @ peak; ASTM D3763 |
| Impact Test | 2.00 J | 1.48 ft-lb | Multiaxial Impact; ISO 6603 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | 260 °C | 500 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| 261 °C @Thickness 3.20 mm |
502 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
Users viewing this material also viewed the following:
- Karina E 850-35/1-C Ivory PVC Compound
- Saint-Gobain CHR® M832 Polyester Film Backing Silicone Adhesive Pressure Sensitive Tape
- Teknor Apex Sinpolene MBB2032 Low Density Polyethylene
- TSE Industries Millathane® HT High Temperature-Resistant Millable Polyester Polyurethane with 70 PHR N220 (ISAF) Filler
- Hexcel® HexForce™ 477 Fiber Glass Fabric
- Arkema Group Orgalloy® RS 6635 A Nylon 66 Alloy, 35% Glass Fiber (Conditioned)
- Bhansali Engineering Abstron KU-600 ABS Super Heat Resistant
- Fainplast Compounds GS 80/T Flexible PVC, Injection Molding for Footwear
- Kazanorgsintez 153-16 Composition of Low Density Polyethylene, Crack-Proof
Copyright © lookpolymers.com All Rights Reserved